Abstract:The rod-like Cr(3)C(2 )micro-whiskers were successfully synthesized from chromic oxide and blank carbon as reaction sources and halide salts and nickel as catalysts by using a carbothermal reduction method assisted with high energy milling and liquid phase catalysis. The optimal preparing condition was to calcine the mixture of Cr2O3:C:NaCl:KCl:Ni = 1:8:0.4:0.4:0.3 (mole ratio) at 1300 degrees C for 2h without other post-treatments. The growth of Cr3C2 micro-whiskers was based on S-L-S mechanism that the brief reaction process of Cr2O3+C -> Cr7C3 -> Cr3C2 occurred in molten catalyst liquids. Besides, the deficiency of carbon led to the generation of Cr7C3 particles, and its excess could induce the formation of coral clusters. The obtained Cr3C2 whiskers were not oxidized in air atmosphere at temperature lower than 1000 degrees C, and a thin Cr2O3 coating which prevented further oxidation gradually formed on the outside of whiskers from 1000 to 1200 degrees C. In addition, the bonding strength of heat resistant adhesive was increased by 16-28% from 500 to 1500 degrees C after adding Cr3C2 whiskers, which was mainly attributed to the pull-out mechanism, whereas the added carbon fibers were completely oxidized and left many sags in adhesive structure, thus severely decreasing the strength. Molecular dynamics simulations with the tersoff forcefield were carried out to facilitate fundamental understanding of the micro-whiskers growing in preferred directions. Combined with theoretical and experimental studies, this work significantly expands the design space and motivates future efforts in exploring the emerging applications of the mechanical properties of Cr3C2 whiskers in severe occasions.

Preparation and Growth Mechanism of TaCx Whiskers

Preparation of different morphology of TaCx whiskers

TiS2 whisker growth by a simple vapor-deposition method

Growth mechanism of Ag(TCNQ) nanocrystal whiskers

The preparation of NbCx whisker

Synthesis Of Nbc Whiskers Having Dendrite Structure

In-Situ Growth of ZnO Whiskers on Ti2ZnC MAX Phases

Thermodynamics and Kinetic Considerations behind the Growth of AlN Whiskers Synthesized by Carbothermal Reduction

Rapid and massive growth of tin whisker on mechanochemically decomposed Ti2SnC

Fabrication and Morphology of Different Color NbCx Whiskers

Ag and Cu Whisker Formation in Ag–Cu–Te Alloys

Morphologies and Growth Mechanisms of Aluminum Nitride Whiskers Synthesized by Carbothermal Reduction

Chromium Carbide Micro-Whiskers: Preparation and Strengthening Effects in Extreme Conditions with Experiments and Molecular Dynamics Simulations

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Effect of Catalyst on the Preparation of Silicon Carbide Whiskers from Silica and Carbon

Preparation and Growth Mechanism of Molybdenum Trioxide Whisker

Whiskers With Apex Angle 135 Degrees Growing By A Disclination Growth Mechanism

A New Growth Technique of Ca-Free&lt;tex&gt;$rm Y_1rm Ba_2rm Cu_3rm O_rm X$&lt;/tex&gt;single-Crystal Whiskers Using Antimony-Doped Precursors

Growth and Microstructure of Aln Whiskers and Dendrites

Crystal Growth of Bi$_{2}$Sr$_{2}$CaCu$_{2}$O$_{8+δ}$ Whiskers from Pulverized Amorphous Precursors

Growth mechanism of Y α-SiAlON whiskers prepared by combustion synthesis