Reactive Sintering of Dual-Phase High-Entropy Ceramics with Superior Mechanical Properties

Sijia Huo,Lei Chen,Xinrui Liu,Qingyi Kong,Yujin Wang,Hui Gu,Yu Zhang

DOI: https://doi.org/10.1016/j.jmst.2022.03.035

2022-01-01

Abstract:Fully dense dual-phase high-entropy ceramics (HECs) were fabricated by hot-pressing at 2000 °C for 1 h based on the in-situ reaction and solid solution processes among equimolar ZrB2, NbB2, HfB2, TaB2 and 30–70 mol% TiC. The negligible porosity, fine grain size, and plate-like diboride grains are found by microstructure observation. The element distribution is not uniform in different phases: Ti and Nb are enriched in the diboride phase, while Zr, Hf, and Ta are preferentially dissolved into the carbide phase. The reactive sintering dual-phase HECs exhibit superior mechanical properties of hardness 28.4 ± 1.5 GPa, flexural strength 1017 ± 91 MPa, elastic modulus 565 GPa, and fracture toughness 4.7 ± 0.3 MPa m1/2, respectively, which surpass most of diboride and carbide high-entropy ceramics in the previous reports.