Abstract:Equimolar quinary diboride powders, with nominal composition of (Ti0.2Hf0.2Zr0.2Nb0.2Ta0.2)B2, were synthesized by boro/carbothermal reduction (BCTR) of oxide mixtures (MOx, M = Ti, Hf, Zr, Nb and Ta) using B4C as source of B and C in vacuum. By adjusting the B4C/MOx ratios, diboride mixtures without detectable MO, were obtained at 1600°C, while high-entropy diboride (HEB) powders with particle size of < 1 µm was obtained at 1800°C. The phase, morphology and solid solution evolution process of the HEB powders during the BCTR process were comprehensively investigated. Although X-ray diffraction pattern indicated the powders synthesized at 1800°C were in a single-phase AlB2 structure, elemental mappings showed that (Ta, Ti)-rich and (Zr, Nb)-rich solid solution coexisted in the HEB powders. The distribution of niobium and zirconium atoms in HEB was unable to reach uniform until the HEB powders were spark plasma sintered at 2000°C. (Ti0.2Hf0.2Zr0.2Nb0.2Ta0.2)B2 ceramics with a relative density of 97.9% were obtained after spark plasma sintering the HEB powders at 2050°C under 50 MPa. Rapid grain growth was found in this composition when the sintering temperature was increased from 2000 to 2050°C, and the averaged grain size increased from 6.67 to 41.2 µm. HEB ceramics sintered at 2000°C had a Vickers hardness of 22.44 ± 0.56 GPa (under a load of 1 kg), a Young's modulus of ∼500 GPa and a fracture toughness of 2.83 ± 0.15 MPa m1/2. This is the first report for obtaining high density HEB ceramics without residual oxide phase, benefiting from the high quality HEB powders obtained.

Fine-grained dual-phase high-entropy ceramics derived from boro/carbothermal reduction

Synergistic hardening in a dual phase high‐entropy (Hf,Nb,Ta,Ti,Zr)C–(Hf,Nb,Ta,Ti,Zr)B2 ultra‐high temperature ceramic

Reactive Sintering of Dual-Phase High-Entropy Ceramics with Superior Mechanical Properties

Highly wear resistant dual-phase (Ti-Zr-Nb-Hf-Ta)C/(Ti-Zr-Nb-Hf-Ta) B2 high-entropy ceramics

Synthesis and Characterization of High-Purity, High-Entropy Diboride Ceramic Powders by a Liquid Phase Method

First-principles prediction, fabrication and characterization of (Hf0.2Nb0.2Ta0.2Ti0.2Zr0.2)B2 high-entropy borides

Microstructures and oxidation mechanisms of (Zr0.2Hf0.2Ta0.2Nb0.2Ti0.2)B2 high-entropy ceramic

Phase, microstructure and related mechanical properties of a series of (NbTaZr)C-Based high entropy ceramics

Low-temperature synthesis and mechanical performance analysis of single-phase high-entropy (Ti,Cr,V,Nb,Ta)B 1.9 ceramics

Hardness of single phase high entropy carbide ceramics with different compositions

Phase stability, mechanical and thermodynamic properties of (Hf, Zr, Ta, M)B 2 (M= Nb, Ti, Cr, W) quaternary high-entropy diboride ceramics via first-principles calculations

A New Route to Fabricate Dual-Phase Compositionally Complex Ceramics

Novel Synthesis of (hf 0.25 Zr 0.25 Ti 0.25 Ta 0.25 )C-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

Thermophysical and mechanical properties of dual-phase medium- and high-entropy rare-earth zirconate ceramics

Preparation of (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C high‐entropy ceramic nanopowders via liquid‐phase precursor

Dense and pure high-entropy metal diboride ceramics sintered from self-synthesized powders via boro/carbothermal reduction approach

Pressureless sintering and properties of (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C high-entropy ceramics: The effect of pyrolytic carbon

Study on microstructure, mechanical properties and thermal performance of single-phase (Ti,Zr,Hf)B 2 solid solution

Microstructures and mechanical properties of high-entropy (Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C ceramics with the addition of SiC secondary phase

Novel Synthesis of (Hf0.25zr0.25ti0.25ta0.25)c-Sic Biphasic Ceramic Micro-Powders Using Single-Source-precursor Route

Dual-Porosity (Ta0.2Nb0.2Ti0.2Zr0.2Hf0.2)C High-Entropy Ceramics with High Compressive Strength and Low Thermal Conductivity Prepared by Pressureless Sintering