Abstract:Nano-scaled pure and iron doping Titanium Dioxide prepared by TiCl4 hydrolysis were obtained. Two methods, step precipitation and co-precipitation, were applied in preparing the iron doping samples. The crystallization and decomposition processes were extensively investigated by methods of X-ray diffraction and TEM. The grain sizes under series of calcinating temperatures were computed according to Voigt function analysis. The results of TEM images also justified the computed grain size. The results showed that Titanium Dioxide prepared by TiCl4 hydrolysis is amorphous, and that no obvious: crystallization temperature or exothermic peaks were observed, contrary to the some previous reports. The computation applying the nuclei growth equation showed that the crystal grain growth of the pure and co-precipitation samples can be divided into 2 steps. The growth activation energy of the former step is 10.7kJ . mol(-1) and 8.6kJ . mol(-1), respectively and that of the latter step is 111.6kJ . mol(-1). As to the step precipitation samples, there showed no obvious difference in crystal growth activation energies for the 2 steps, and for the transformation of anantase to rutile was almost completed before 600 degrees C. There was evidence that the iron doping accelerated the transformation of rutile to anatase and this is especially obvious in step precipitation samples.

Preparation of Rutile TiO<sub>2</sub> Film by Low Temperature Hydrothermal

Low-temperature deposition of ultrafine rutile TiO2 thin films by the hydrothermal method

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Low‐Temperature Growth of Monolayer Rutile TiO2 Nanorod Films

Preparation of TiO2 films under low temperature condition on the glass substrate

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Low‐Temperature Growth of Rutile Nanorod Thin Films and Their Photon‐Induced Property

One-step Hydrothermal Synthesis of Suprastructural Rutile (Α-Tio2) with Controllable Morphology in Microemulsions at Low Temperature

PREPARATION OF ROD-LIKE RUTILE TiO2 BY SOL-HYDROTHERMAL METHOD

Low-temperature preparation of titania nanorods through direct oxidation of titanium with hydrogen peroxide

A Novel Method for Preparation of Nanocrystalline Rutile TiO2 Powders by Liquid Hydrolysis of TiCl4

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Low‐Temperature Preparation of Anatase and Rutile Layers on Titanium Substrates and Their Ability to Induce in Vitro Apatite Deposition

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

Synthesis of Rutile Nanoparticles by Microemulsion Method at Low Temperature

Synthesis of Nanosized Rutile TiO2 Powder at Low Temperature

Large-scale Synthesis and Characterization of Fan-Shaped Rutile TiO2 Nanostructures

Preparation of TiO2 Thin Films at Low Temperature and Characterization of Their Properties

Photoelectrocatalytic Efficiency of Low-Temperature Precipitated Monolayer Rutile TiO 2 Nanoflower Film

Hydrothermal preparation of BaTiO3 thin film on silicon

Fabrication of ordered macroporous rutile titania at low temperature

Preparation of Rutile TiO&lt;sub&gt;2&lt;/sub&gt; Film by Low Temperature Hydrothermal