Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Fabrication and Properties of AlN-SiC Multiphase Ceramics <i>via</i> Low Temperature Reactive Melt Infiltration

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

High strength C/Si‒Ni‒C composites fabricated by reaction melt infiltration with Si‒Ni alloy at lower temperature

Preparation and mechanical properties of SiC-AlN ceramic alloy

Pressureless Infiltration Preparation of High SiC/Al Ceramic Matrix Composites

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering

Mechanical Properties of SiC-AlN Single-Phase Alloys and Two-Phase Composites.

Fabrication and Mechanical Properties of Si3N4/SiC Nanocompoisites under Pressureless Sintering.

Fabrication, Microstructure, and Properties of SiC/Al 4 SiC 4 Multiphase Ceramics Via an In-Situ Formed Liquid Phase Sintering

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

Fabrication, microstructure, and properties of SiC/Al4SiC4 multiphase ceramics via an in-situ formed liquid phase sintering

Study on the mechanical properties and microstructure of Al2O3/nano-SiC multiphase ceramics

Study on In-Situ Reaction Synthesis and Mechanical Properties of Si2N2O Ceramic

Fabrication of C/SiC composites by siliconizing carbon fiber reinforced nanoporous carbon matrix preforms and their properties

SiC Nanoparticles Strengthened Alumina Ceramics Prepared by Extrusion Printing

Phase Transformation, Microstructure and Mechanical Properties of Si3n4/Sic Composite

In-situ formation of bulk and porous h-AlN/SiC-based ceramics from geopolymer technique

Enhanced mechanical properties of R–SiC honeycomb ceramics with in situ AlN–SiC solid solution

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Fabrication and Properties of SiC/mullite Composite Porous Ceramics

Preparation, microstructure and ion-irradiation damage behavior of Al4SiC4-added SiC ceramics