Abstract:The effects of casting and different heat treatment processes on the corrosion resistance of AlFeCoNiMo0.2 high-entropy alloy in 3.5% NaCl (mass fraction) and 0.5 mol/L H2SO4 solutions were investigated using dynamic potential polarization curves, SEM, XRD, XPS, and other test methods. The results show that in the Cl− environment, the cast alloy has the lowest corrosion current density and higher corrosion resistance compared to the annealed alloy. The elements Al and Mo are severely segregated in the crystal and in the grain boundaries, where galvanic corrosion occurs, and the Al-rich phase produces pitting corrosion in the crystal. The main components of its passive film are oxides of Al, Fe, Co, and Mo, and oxides and hydroxides of Ni. In the SO42− environment, the best corrosion resistance is achieved in the 900 °C annealed state of the alloy. Electrochemical test results show that the alloys all undergo secondary passivation, producing two successive product films to protect the metal matrix. Preferential corrosion areas are concentrated in the molybdenum-rich grain boundaries and nearby dendritic regions, reducing the corrosion resistance of the alloy. The main components of the passive film are oxides of Al and Mo; oxides of Fe, Co, Ni; and hydroxides. The Mo element in the passive film prevents the activated dissolution of Fe and produces the protective component MoO3, which inhibits the dissolution of the alloy and improves the stability of the passive film. The presence of Mo elements increases the selective dissolution of Fe, and the aggregation of Mo elements at grain boundaries after annealing weakens the corrosion resistance of the alloy and leads to the dissolution of the passive film. The main components of the passive film are oxides of Al and Mo; oxides of Fe, Co, Ni; and hydroxides.

Effect of oxide layer on the electrochemical corrosion behavior of a Ni-based superalloy in 3.5 wt% NaCl

Electrochemical Behaviors of Ni-Base Superalloy CMSX-4 in 3.5 wt.% NaCl: Effect of Temperature and Preoxidation

Effects of processing parameters on the surface quality of wrought Ni-based superalloy by ultrasonic-assisted electrochemical grinding

Optimizing the surface quality of electrochemical machined Ni-based single crystal superalloy via manipulation of phase and dendrite dissolution

Effects of Different Surface Native Pre-Oxides on the Hot Corrosion Properties of Nickel-Based Single Crystal Superalloys

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

Effect of Heat Treatment on the Corrosion Resistance of AlFeCoNiMo0.2 High-Entropy Alloy in NaCl and H2SO4 Solutions

Electrochemical surface modification of GH4742 nickel-based superalloy in C6H5Na3O7 solution

Corrosion Behavior of Pre-oxidized GH4169 Alloy with Solid NaCl Deposited in a Wet Oxygen Flow at 600 °C

Hot Corrosion Behaviour of Electroless Deposited Nano-structured Cerium Oxide Coatings on Superalloy

Compound purification of nickel base superalloy cutting waste through special cleaning agent attached to ultrasonic stirring

Corrosion behavior of AlCoCrFeNi2.1 eutectic high-entropy alloy in Cl--containing solution

Effect of Aging Time on the Corrosion Behavior of a Cu-Ni-Si Alloy in 3.5 wt% NaCl Solution

Probing the tribocorrosion behaviors of three nickel-based superalloys in sodium chloride solution

Investigation of electrochemical dissolution behavior of Ni(γ)/Ni3Al(γ') and Co(γ)/Co3Al(γ') superalloys in NaNO3 solution

Electrochemical study on the hot corrosion behavior of Ni16Cr13Co4Mo alloy in molten NaCl-KCl and NaCl-KCl-Na2SO4

Influence of temperature on hot corrosion behavior of GH4169 superalloy subjected to Na 2 SO 4 -NaCl salts attack

Investigation on the hot corrosion behavior of a single crystal Ni-based superalloy in molten Na2SO4+K2SO4 salts improved by different preoxidation treatments

Effect of Ni on the oxidation behavior of corrosion products that form on low alloy steel exposed to a thin electrolyte layer environment

Competitive oxidation behavior of Ni-based superalloy GH4738 at extreme temperature

Hot corrosion of sputtered nanocrystalline coating with and without preoxidation and arc ion plating coating on a Ni-based single-crystal superalloy