Abstract:The hot corrosion behaviour of plasma sprayed WC-CoCr coatings on AISI 316L steel substrate is studied in two corrosive salt environments namely 100% Na2SO4 and 75% Na2SO4+25%NaCl at 1000 °C. Also, on WC-CoCr coated AISI 316L steel substrate, a persistent Cr2O3 barrier scale is created employing pre-oxidation at 1200 °C for ten hours with the expectation that it would withstand hot corrosion in a Na2SO4 salt environment at 900 °C. X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), electron micro probe analysis (EPMA) and scanning electron microscopy (SEM) are performed on samples to examine the pre oxidation and hot corrosion characteristics of plasma sprayed WC-CoCr coatings at elevated temperatures. The findings indicate that the presence of both salt environment affects the degradation process of WC-CoCr coatings. The coatings in 100% Na2SO4 and the mixture of 75% Na2SO4+25%NaCl has a weight change of 0.14 mg/cm2 and 0.33 mg/cm2, respectively, after hot corrosion at 1000 °C for 50 cycles. Each cycle includes 1 hour heating in furnace and 20 minutes cooling in ambient air. Corrosion kinetics using thermogravimetric method showed that non-pre-oxidized samples gained 52.5 % more weight and more severely affected by hot corrosion than pre-oxidized ones. During hot corrosion after 2 hours, there was relatively negligible corrosion, but after 4 and 8 hours, deposits of Na2WO4, WO3, Cr2O3 and CoSO4 were produced. Oxides were primarily composed of Cr2O3 and WO3. Cr2O3 and WO3 acted as barriers to the penetration and diffusion of corrosive elements through coatings, which contributed to the hot corrosion resistance in the corrosive area. The hot corrosion deterioration of WC-CoCr coatings may be effectively reduced by introducing pre oxidation. Slower reaction rate of pre oxidized Cr2O3 scale may operate as a barrier which separates hot corrosion by Na2SO4 salt.

Hot Corrosion Behaviour of Electroless Deposited Nano-structured Cerium Oxide Coatings on Superalloy

Electroless nanoceria films on nickel-based superalloy

Corrosion behavior and failure mechanism of amorphous Al2O3 coating at high-temperature LBE

Effect of CeO2 Coating on the Isothermal Oxidation Behaviour of Ni-Based Alloy 230

Corrosion inhibition analysis on cerium induced hydrophobic surface of Al-6061/SiC/Al2O3 hybrid composites

Electrochemical Study of Corrosion Behavior of Rare Earth Based Chemical Conversion Coating on Aerospace Aluminum Alloy

Microstructural Features, Corrosion and Wear Behavior of the AlCrFeCoNiCu High-Entropy Alloy, Electrodeposited Coatings, and Subsequent Heat Treatment

Hot Corrosion and Electrochemical Behavior of NiCrAlY, NiCoCrAlY and NiCoCrAlYTa Coatings in Molten NaCl-Na2SO4 at 800 °C

Electrochemical corrosion resistance of aluminum alloy 6101 with cerium-based coatings in an alkaline environment

Hot corrosion of sputtered nanocrystalline coating with and without preoxidation and arc ion plating coating on a Ni-based single-crystal superalloy

Surface morphological studies on hot corrosion behaviour of pre-oxidized plasma sprayed WC-CoCr coating on AISI316L steel in Na 2 SO 4 /NaCl molten salt environment

Electrochemical and hot corrosion behaviour of annealed AlCoCrFeNi HEA coating over steel

Preparation and Corrosion Behaviour of Cerium Based Sol-gel Composite Coatings on AA2024-T4 Aluminum Alloy

Corrosion Performance of Nano-Alumina Coatings over Anodized Aluminum Alloy by Dip Coating Method

Co-electrodeposition of superhydrophobic NiCo/CeO 2 coating with hierarchical nano/micro structure for corrosion protection of plain carbon steel

Influence of Heat Treatment on Microstructural, Corrosion and Tribological Behaviour of Electrodeposited AlCoFeMnNiCu High Entropy Alloy Coatings

The preparation of cerium nitrate and attapulgite based superhydrophobic epoxy coatings for the corrosion protection of Q355 mild steel surface

Preparation and hot corrosion properties of the AlCrFeCoNi0.5Si high-entropy alloy coating deposited by the air plasma spraying

Influence of the Chemical Composition of Ceria Conversion Coatings, Sealed in Solution of NaH2PO4 and Ca(NO3)2, on the Corrosion Behavior of Aluminum

High-Temperature Corrosion of APS- and HVOF-Coated Nickel-Based Super Alloy under Air Oxidation and Melted Salt Domains

Microstructural evolution and high temperature hot corrosion behaviour of AlCoCrFeNiTi high-entropy alloy coatings