Corrosion Performance of Nano-Alumina Coatings over Anodized Aluminum Alloy by Dip Coating Method

Dalip Singh,Veena Dhayal,Dinesh Chandra Agarwal

DOI: https://doi.org/10.3103/S1068375519040148

2019-11-25

Surface Engineering and Applied Electrochemistry

Abstract:Alumina coatings are widely used to enhance the wear, abrasion, and corrosion resistance of metal components. This investigation aims at studying the alumina sol-gel coating on the anodized aluminum alloy surface using a dip coating technique. A stable alumina coating was deposited over the anodized aluminum surface using oxime-modified aluminum(III) isopropoxide as sol-gel precursor. The scanning electron microscopy image of the coated anodized sample suggests deposition of a uniform and crack-free aluminum coating. The corrosion resistances of bare, anodized, and coated anodized aluminum alloy samples were investigated by electrochemical impedance spectroscopy and potentiodynamic polarization in 3.5 wt % aqueous NaCl solution. An appreciable shifting was observed in the equilibrium corrosion potential ( E corr ) and the corrosion current density ( i corr ) values of both anodized and coated anodized samples: i.e. E corr : from –1377.11 mV (anodized) to –711.54 mV (coated anodized) and i corr : from 80.37 μA/cm 2 (anodized) to 0.090 μA/cm 2 (coated anodized). The results clearly indicate the corrosion resistive behavior of nano-alumina coatings.

English Else