Effect of Aging Time on the Corrosion Behavior of a Cu-Ni-Si Alloy in 3.5 wt% NaCl Solution

Qian Lei,Zhou Li,Liang Han,Zhu Xiao,Tao Xiao
DOI: https://doi.org/10.5006/1884
2016-05-01
CORROSION
Abstract:Effect of aging time on corrosion behavior of a Cu-6.0Ni-1.0Si-0.5Al-0.15Mg-0.1Cr alloy immersed in a 3.5 wt. % NaCl solution was investigated. The studied alloy exhibits good corrosion resistance comparing with other super high strength Cu-based alloys, and the corrosion resistance increases with the aging time. The purity of the copper matrix increases with precipitation and precipitates coarsening, as a result that the corrosion resistance increases. Impedance spectra and equivalent circuit analysis confirms that a multi-layer protective film formed on sample surface. Typical uniform corrosion appeared in this alloy, and the film density increased with the immersion day and the aged-treated time. X-ray photoelectron spectra results shows that the main corrosion products are CuO, Cu2O, Al2O3 and Al(OH)3.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?