Abstract:Bearing steel (GCr15) is widely used in key parts of mechanical transmission for its excellent mechanical properties. Electrochemical machining (ECM) is a potential method for machining GCr15, as the machining process is the electrochemical dissolution of GCr15 regardless of its high hardness (>50 HRC). In ECM, NaNO3 solution is a popular electrolyte, as it has the ability to help in the nonlinear dissolution of many metallic alloy materials, making it useful for precision machining. However, due to high carbon content of GCr15, the electrochemical dissolution of GCr15 is unique, and there is always a black layer with high roughness on the machined surface, reducing the surface quality. In order to improve the electrochemical machining of GCr15 with a high surface quality, the surface characteristics of GCr15 in ECM were investigated. The anodic polarisation curve in the NaNO3 electrolyte was measured and electrochemical dissolution experiments were conducted with different current densities. SEM, XRD, and XPS were employed to analyse the surface morphology and composition formed on the machined surface at different current densities. The initial results showed that there were two parts (black part and bright part) formed on the machined surface when a short circuit occurred, and the test results suggested that the black part contained a mass of Fe3O4 while the bright part was composed of mainly Fe and Fe3C. Further investigation uncovered that a black flocculent layer (Fe3O4) always formed in a low current density (32 A/cm2) with high roughness. With the current density increased, the amount of black flocculent layer was reduced, and Fe3C particles appeared on the machined surface. When the current density reached 81 A/cm2, the entire flocculent oxide layer was removed, only some spherical Fe3C particles were inserted on the machined surface, and the roughness was reduced from Ra7.743 μm to Ra1.783 μm. In addition, due to exposed Fe3C particles on the machined surface, the corrosion resistance of the machined surface was significantly improved. Finally, circular arc grooves of high quality were well manufactured with current density of 81 A/cm2 in NaNO3 electrolyte.

Effects of processing parameters on the surface quality of wrought Ni-based superalloy by ultrasonic-assisted electrochemical grinding

Study on Ultrasonic Assisted Electrochemical Drill-Grinding of Superalloy

Fundamental Machining Characteristics of Ultrasonic-Assisted Electrochemical Grinding of Ti–6Al–4V

Study on Grinding Force and Surface Roughness of Ni3Al Based Superalloy

Electrochemical surface modification of GH4742 nickel-based superalloy in C6H5Na3O7 solution

Experimental and FEM study of surface modification of nickel-based superalloy subjected to ultrasonic surface rolling process

Anodic Dissolution Behavior of DD6 Nickel-Based Single Crystal Superalloy for Electrochemical Machining Applications

Study of machining performance for electrochemical grinding of difficult-to-cut alloy U71Mn

Investigations on surface modification of nickel-based superalloy subjected to ultrasonic surface rolling process

Optimizing the surface quality of electrochemical machined Ni-based single crystal superalloy via manipulation of phase and dendrite dissolution

Workpiece Surface Integrity of GH4169 Nickel-Based Superalloy when Employing Abrasive Belt Grinding Method

A study on ultrasonic assisted grinding of nickel-based superalloys

System Design and Mechanism Study of Ultrasonic-Assisted Electrochemical Grinding for Hard and Tough Materials

Anodic dissolution behavior of the complex microstructure of laser directed energy deposited Alloy 718 during electrolyte jet machining in NaCl-ethylene glycol electrolyte

Surface Integrity of Nickel-Base Superalloy Materials by Electric Hot Machining

Compound purification of nickel base superalloy cutting waste through special cleaning agent attached to ultrasonic stirring

Electrochemical Machining of Micro-Pit Arrays on a GH4169 Alloy with a Roll-Print Mask Using a C6H5Na3O7-Containing NaNO3 Mixed Electrolyte

Investigation of the Surface Characteristics of GCr15 in Electrochemical Machining

Effects of grinding parameters on surface integrity of GH4169 nickel-based superalloy

Experimental Study on Ultrasonic Assisted Turning of GH4068 Superalloy

Effect of oxide layer on the electrochemical corrosion behavior of a Ni-based superalloy in 3.5 wt% NaCl