Ablation Property of Tungsten Nozzle Produced by Plasma Spray Forming

Xin Min

2011-01-01

Abstract:The tungsten nozzle with inner diameter of 8 mm,length of 30 mm and wall thickness of 16.5 mm was produced by plasma spray forming(PSF) and hot isostatic pressing(HIPing).The resistance of thermal shock and ablation property of tungsten throat was investigated by firing test on a small solid rocket motor(SRM).The results show that a lamellar structure consisting of vertical columnar grains is found in PSF deposits with relative density of 85.6%.After two-step HIPing,the relative density of deposits remaining lamellar structure increases to 96.7%.After firing testing,the specimen has entire form and no breaks,which indicates that tungsten nozzle has good resistance to thermal shock and ablation.The line ablation rate of throat is only 4 μm/s.From results of scanning electron microscopy(SEM) and X-ray diffractometer(XRD),the ablation of throat is the most serious for combinative results of mechanical denudation,melt ablation and thermochemistry ablation.The second serious ablation is convergence part,the ablation behaviors of which are mechanical denudation and melt ablation.While the ablation content of dilation part is the slightest for only thermochemistry ablation taking place.