Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Hydrothermal Synthesis and Characterization of Ce_(0.6)Zr_(0.4)O_2 and BaSO_4 Micro/Nano-particles

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Synthesis and Characterization of Mesostructured Ceria-Zirconia Solid Solution

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Hydrothermal synthesis of tin doped ceria-zirconia solid solutions with enhanced thermal stability and oxygen storage capacity

Preparation of La2o3-Doped Ceo2-Zro2 Solid Solution with High Thermal Stability by Water-In-Oil Microemulsion

Hydrothermal Preparation of Mesoporous Ce0.5Zr0.5O2 Solid Solution with High Surface Area by PEG Template

Characterization and Application of Nanometer Ce_(0.75)Zr_(0.25)O_2 Powder Synthesized by Solid State Chemical Reaction Method

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Hydrothermal synthesis of CeO2 nano-particles

Preparation of Mesoporous Ce0.5Zr0.5O2 Mixed Oxide by Hydrothermal Templating Method

Controllable synthesis of (Ba0.85Ca0.15)(Zr0.1Ti0.9)O3 submicron sphere by hydroxide co-precipitation method

Synthesis and Characterization of Wormhole-Like Mesoporous Ce0.6Zr0.35Y0.05O2 Solid Solutions

Characterization of Cerium-Zirconium Solid Solutions Prepared by the Microwave-Assisted Approach

Preparation of Ceria-Zirconia Solid Solution by Urea-Based Hydrothermal-Copricipitation Method and its Catalytic Application

Preparation of Ultrafine Ce-Zr-Ba Mixed Oxide Powder with High Surface Area

Effects of ceria/zirconia ratio on properties of mixed CeO2-ZrO2-Al2O3 compound

Hydrothermal Synthesis of Stable Mesoporous ZrO2–Y2O3 and CeO2–ZrO2–Y2O3 from Simple Inorganic Salts and CTAB Template in Aqueous Medium

Synthesis of Nanostructured Ceria, Zirconia and Ceria–zirconia Solid Solutions Using an Ultrahigh Surface Area Carbon Material As a Template

Preparation and characterization of high specific surface area Ce 0.5Zr0.5O2 mixed oxide

Facile Synthesis of High Surface Area Nanostructured Ceria-Zirconia-yttria-lanthana Solid Solutions with the Assistance of Lauric Acid and Dodecylamine