Abstract:Mesoporous Ce0.2Zr0.8O2 nanosized powders were synthesized via a hydrothermal method in the presence of urea without any templates using a trivalent cerium salt as the starting material. The analyses by medium-angle powder X-ray diffraction (PXRD) and vis-Raman spectroscopy showed that the Ce0.2Zr0.8O2 powders were solid solutions of pure tetragonal phase, whether as-prepared at 160degreesC or calcined at 773-1273 K. By low-angle PXRD and transmission electron microscopy, the as-prepared Ce0.2Zr0.8O2 showed a short-range ordered mesostructure probably as a result of the natural agglomeration of uniform nanoparticles upon hydrothermal treatment. The as-prepared powders had high surface areas (232-281 m(2) g(-1)) and narrow pore size distributions (3.5-4.0 nm), according to the measurements of nitrogen adsorption. After calcining at 773 K, this mesostructure was retained to some degree with lower surface areas (66-75 m(2) g(-1)) and larger pore sizes (5.1-7.2 nm). Determined by X-ray photoelectron spectroscopy, the numbers of oxygen vacancies (0.025-0.037) on the nanocrystalline surface was high for both as-prepared and calcined Ce0.2Zr0.8O2. UV-vis absorption measurements showed that the band gap energy of the as-prepared Ce0.2Zr0.8O2 nanocrystals was distinctly blue-shifted compared with the bulk value due to the quantum size effect. The catalytic tests demonstrated that the Ce0.2Zr0.8O2 nanosized powders synthesized at 160degreesC showed higher thermal stability in terms of surface area and phase composition, and higher catalytic activity for CO conversion than that synthesized at 140degreesC. Among all the catalysts tested, the mesostructured one with the highest surface area and the largest pore volume displayed the highest oxygen storage capacity of 233 mumol CO g(-1) at 773 K, and the lowest 50% conversion temperature of 641 K.

Synthesis of Nanostructured Ceria, Zirconia and Ceria–zirconia Solid Solutions Using an Ultrahigh Surface Area Carbon Material As a Template

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Synthesis and characterization of ceria nanoparticles by complex-precipitation route

Dimension-Manipulated Ceria Nanostructures (0d Uniform Nanocrystals, 2d Polycrystalline Assembly, and 3d Mesoporous Framework) from Cerium Octylate Precursor in Solution Phases and Their Co Oxidation Activities

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Hydrothermal Synthesis of Stable Mesoporous ZrO2–Y2O3 and CeO2–ZrO2–Y2O3 from Simple Inorganic Salts and CTAB Template in Aqueous Medium

Synthesis and Characterization of Nanoscaled Cerium (IV) Oxide Via a Solid‐State Mechanochemical Method

Preparation and Characterization of Ceria-Zirconia Ceramics Using a Sol-Gel Process

Preparation of Ultrafine Ce-Zr-Ba Mixed Oxide Powder with High Surface Area

Ultrafast, Continuous and Shape-Controlled Preparation of CeO2 Nanostructures: Nanorods and Nanocubes in a Microfluidic System

Synthesis and Characterization of Zirconium Nitride Nanopowders by Internal Gelation and Carbothermic Nitridation

Synthesis of Doped Ceria–zirconia Core–shell Nanocomposites Via Sol–gel Process

Non-Template Hydrothermal Route Derived Mesoporous Ce0.2zr0.8o2 Nanosized Powders With Blue-Shifted Uv Absorption And High Co Conversion Activity

Facile Synthesis of Zr-Based Functional Materials with Highly Ordered Mesoporous Structures

Synthesis, structure and porosity analysis of microporous and mesoporous carbon derived from zirconium carbide

Facile Alcohothermal Synthesis, Size-Dependent Ultraviolet Absorption, and Enhanced CO Conversion Activity of Ceria Nanocrystals

Combustion Synthesis of Zirconium-Doped Ceria Nanocatalyst

Shape-Controlled Synthesis And Catalytic Application Of Ceria Nanomaterials

Structure, synthesis, and catalytic properties of nanosize cerium-zirconium-based solid solutions in environmental catalysis

High Surface Area Ceria Nanoparticles via Hydrothermal Synthesis Experiment Design