Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Hydrothermal synthesis of CeO2 nano-particles

Synthesis and Crystallization of Nano-Ceria Particles by Solvothermal Routes

Microwave-assisted Synthesis of Ceria Nanoparticles

Controlled Hydrothermal Synthesis of CeO2 Nanoparticles, Their Photocatalytic Activity and Room Temperature Ferromagnetism

Preparation of nano-sized CeO2 by mechanochemical reaction of cerium carbonate with sodium hydroxide

Synthesis and Characterization of Nano Cerium Oxide Using Hydrothermal Technique

Batch Supercritical Hydrothermal Synthesis of Ceo2 Nanoparticles

Template-free Hydrothermal Synthesis and Characterisation of Single Crystalline Ce(OH)CO 3 and CeO 2 with Spindle-Like Structures

Synthesis and characterisation of CeO2 nanoparticles and rods

Solvent Assisted Morphology-Controlled Synthesis of CeO2 Micro/nanostructures

Synthesis and Performance of CeO2 Nanocrystallines by Precipitation Method

Solvothermal Synthesis of Titania/ceria

Formation and Thermal Decomposition of Cerium‐Organic Precursor for Nanocrystalline Cerium Oxide Powder Synthesis

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Controllable Synthesis, Characterization, and CO Oxidation Activity of CeO 2 Nanostructures with Various Morphologies

Fast Synthesis Of Cerium Oxide Nanoparticles And Nanorods

Self-template hydrothermal synthesis of CeO2 hollow nanospheres

Hydrothermal Process Characterization of CeO_2/ZnO Composite Nanostructure

Hydrothermal Synthesis of CeO2nanorods Using a Strong Base–weak Acid Salt As the Precipitant

Shape-controlled synthesis of CeOHCO3 and CeO2 microstructures

Synthesis of CeO2 and Co3O4 Nanoparticles