Abstract:Novel slight yellow CeO2single/multiwall hollow microspheres were synthesized by the hydrothermal method without any surfactant and characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), field-emission scanning electron microscopy (FESEM), and x-ray photoelectron spectra (XPS). The results showed that the products were CeO2single/multiwall hollow microspheres, the shells of which were composed of CeO2nanoparticles with a mean size of 70 nm. The effect of the preparation conditions, the reaction temperature, the reaction time, and the molar ratios of urea to Ce(NO3)3·6H2O on the morphology of the products, was investigated. The optimal preparation conditions are determined as follows: the reaction temperature of 230 °C, the reaction time of 6 to 10 h, and the molar ratios of urea to Ce(NO3)3·6H2O of 3:1 to 6:1. The formation mechanism of CeO2single/multiwall hollow microspheres was proposed. The ultraviolet-visible (UV-VIS) diffuse reflectance spectra of the samples were measured. The results showed that the absorption edges of the samples were red-shifted compared with that of bulk CeO2, and that the red-shift of the absorption edges and the yellow of the samples enhanced with increasing the yield of CeO2single/multiwall hollow microspheres. The catalytic activity and the recycling performance of the sample on CO oxidation were tested and theT100%(the temperature at which CO 100% conversion) was 230 °C in the first run and decreased by 270 and 205 °C compared with that of bulk CeO2and CeO2nanocrystal, respectively.

Synthesis and Characterization of Ceo2 by the Hydrothermal Method Assisted by Carboxymethylcellulose Sodium

Study on Catalytic Performance and Kinetics of High Efficiency CeO2 Catalyst Prepared by Freeze Drying for the Synthesis of Dimethyl Carbonate from CO2 and Methanol

Study of the Preparation and Properties of CeO2single/multiwall Hollow Microspheres

Hydrothermal synthesis of CeO2 nano-particles

Highly uniform CeO2 hierarchical microstructures: Facile synthesis and catalytic activity evaluation

Study on synthesis and modification of Ti/Ce composite oxide

Morphology-controlled Synthesis, Characterization and Microwave Absorption Properties of Nanostructured 3D CeO 2

Shape-controlled synthesis of CeOHCO3 and CeO2 microstructures

Preparation and Characterization of CeO<sub>2</sub> with Different Particle Sizes and Morphology

Synthesis and characterisation of CeO2 nanoparticles and rods

Preparation of nano-sized CeO2 by mechanochemical reaction of cerium carbonate with sodium hydroxide

Synthesis of Biomorphic Hierarchical Ceo2 Microtube with Enhanced Catalytic Activity

Synthesis of Mesoporous CeO2-MnOx Binary Oxides and Their Catalytic Performances for CO Oxidation

Hierarchical Organization and Catalytic Activity of High-Surface-area Mesoporous Ceria Microspheres Prepared Via Hydrothermal Routes.

Hydrothermal Preparation and Oxygen Storage Capacity of Nano CeO2-based Materials

Preparation and characterization of CeO2 with different particle sizes and morphology

Synthesis, Characterization And Application Of Ce-Mcm-48 As A Mesoporous Molecular Sieve

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

Hydrothermal synthesis of CeO 2 nanoparticles on activated carbon with enhanced desulfurization activity

Facile Synthesis Of 3d Flowerlike Ceo2 Microspheres Under Mild Condition With High Catalytic Performance For Co Oxidation

Textural, Structural, and Morphological Characterizations and Catalytic Activity of Nanosized CeO2–MOx (M = Mg2+, Al3+, Si4+) Mixed Oxides for CO Oxidation