Abstract:Uniform ceria nanocrystals with good crystallinity and high surface areas were prepared by a facile alcohothermal method with the addition of bases (KOH or NaOH), using Ce(III) or Ce(IV) salt as a starting material. The as-prepared nanocrystals were characterized by means of powder X-ray diffraction (PXRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), nitrogen adsorption, thermogravimetry and differential thermal analysis (TG-DTA), Fourier transformation infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and ultraviolet and visible spectroscopy (UV-vis). The ceria crystals had controllable sizes from 2.6 to 6.9 nm estimated by the PXRD line broadening analysis. TEM and HRTEM micrographs showed that the as-prepared ceria nanocrystals have a relatively high degree of crystallinity and low degree of conglomeration under high base concentrations. BET specific surface areas of the as-synthesized ceria nanocrystals were very high (103-238 m(2) g(-1)). XPS spectra indicated that the cerium in the nanocrystals was predominantly tetravalent. UV-vis spectra revealed that both the direct and indirect band gap energies of the as-prepared ceria nanocrystals showed a pronounced blue-shifting due to the quantum confinement effect compared to bulk ceria. And the dielectric confinement effect on the band gap energies was also discussed. The as-prepared ceria nanocrystals supported on gamma-Al2O3 exhibited a rather lower conversion temperature (559 K) for CO oxidation to CO2 than that of bulk catalysts prepared by the coprecipitation method. Finally, a hydrolytic alcohothermal mechanism for the preparation of ceria nanocrystals was forwarded.

Highly uniform CeO2 hierarchical microstructures: Facile synthesis and catalytic activity evaluation

Hierarchical Organization and Catalytic Activity of High-Surface-area Mesoporous Ceria Microspheres Prepared Via Hydrothermal Routes.

Synthesis of Biomorphic Hierarchical Ceo2 Microtube with Enhanced Catalytic Activity

A Facile Synthesis for Hierarchical Porous CeO2 Nanobundles and Their Superior Catalytic Performance for CO Oxidation

Shape-controlled synthesis of CeOHCO3 and CeO2 microstructures

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

Facile Synthesis Of 3d Flowerlike Ceo2 Microspheres Under Mild Condition With High Catalytic Performance For Co Oxidation

Facile Alcohothermal Synthesis, Size-Dependent Ultraviolet Absorption, and Enhanced CO Conversion Activity of Ceria Nanocrystals

Controllable Synthesis, Characterization, and CO Oxidation Activity of CeO 2 Nanostructures with Various Morphologies

Shape Effect of Microstructured CeO2 with Various Morphologies on CO Catalytic Oxidation

Synthesis of a hierarchical SiO2/Au/CeO2 rod-like nanostructure for high catalytic activity and recyclability

Synthesis Of A Hollow Ceo2/Au/C Hierarchical Nanostructure For High Catalytic Activity And Recyclability

Gold and Cuo Nanocatalysts Supported on Hierarchical Structured Ce-Doped Titanias for Low Temperature Co Oxidation

Template-free Synthesis of Hierarchical Layer-Stacking CeO2 Nanostructure with Enhanced Catalytic Oxidation Activity

Mesoscale organization of nearly monodisperse flowerlike ceria microspheres.

Dimension-Manipulated Ceria Nanostructures (0d Uniform Nanocrystals, 2d Polycrystalline Assembly, and 3d Mesoporous Framework) from Cerium Octylate Precursor in Solution Phases and Their Co Oxidation Activities

In-situ Fabrication of Ce-rich CeO2 Nanocatalyst for Efficient CO Oxidation

Template-free Hydrothermal Synthesis and Characterisation of Single Crystalline Ce(OH)CO 3 and CeO 2 with Spindle-Like Structures

Unraveling the Interaction Between Fe and CeO2(111) Through Growth, Structure, and Thermal Stability Studies

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Facile Synthesis and Catalytic Properties of CeO2 with Tunable Morphologies from Thermal Transformation of Cerium Benzendicarboxylate Complexes