Abstract:Ce1-xZrxO2 (x = 0-0.8) nanoparticulate powders were prepared via a mild urea hydrolysis based hydrothermal method through homogeneous nucleation at 413 K followed by calcination at 773 or 1173 K. X-ray fluorescence (XRF) and energy-dispersive X-ray analysis (EDAX) measurements testify to the good stoichiometric homogeneity of Ce and Zr cations in the as-obtained Ce1-xZrxO2 products. X-ray photoelectron spectroscopy (XPS) and ultraviolet-visible (UV-vis) spectra exhibit that both surface and bulk ratios of Ce3+ to Ce4+ for the as-prepared Ce1-xZrxO2 nanocrystals increased with the zirconium content x. Powder X-ray diffraction (PXRD) patterns and Raman spectra demonstrate that the present Ce1-xZrxO2 samples were single-phase solid solutions with good structural homogeneity and high thermal stability up to 1273 K, and those with x = 0.4-0.6 retained a pseudocubic structure (t" phase) due to the small crystallite size effect. Transmission electron microscopy (TEM) micrographs reveal that the as-prepared CeO2-ZrO2 nanocrystals were highly crystallized with narrow size distribution. Nitrogen adsorption measurements show that the BET specific surface areas of the Ce1-xZrxO2 powders were improved by the incorporation of ZrO2. The PXRD data and high-resolution TEM (HRTEM) images illuminate that the as-prepared and as-calcined Ce1-xZrxO2 (x = 0.4-0.6) powders kept a rather high strain level in the crystal lattice. The lattice strains in our Ce1-xZrxO2 catalysts show a linear relationship with their oxygen storage capacity (OSC) values. This linear correlation is explained on the basis of qualitative structural and defective analysis, and might find use in the screening and design of better-performing three-way catalysts (TWCs). The highest CO-OSC values of the studied CeO2-ZrO2 catalysts appeared for Ce0.5Zr0.5O2 (543 mumol of CO g(-1) at 773 K and 628 mumol of CO g(-1) at 973 K).

Hydrothermal synthesis of tin doped ceria-zirconia solid solutions with enhanced thermal stability and oxygen storage capacity

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Hydrothermal synthesis and automotive exhaust catalytic performance of CeO2 nanotube arrays

Hydrothermal Preparation and Oxygen Storage Capacity of Nano CeO2-based Materials

Urea-Based Hydrothermally Derived Homogeneous Nanostructured Ce1-Xzrxo2 (X=0-0.8) Solid Solutions: A Strong Correlation Between Oxygen Storage Capacity and Lattice Strain

In-situ Formed Stable Pt Nanoclusters on Ceria-Zirconia Solid Solutions Induced by Hydrothermal Aging for Efficient Low-Temperature CO Oxidation

Hydrothermal synthesis of CeO2 nano-particles

Nanocrystalline Ce1−xSmxO2−δ (x = 0.4) solid solutions: structural characterization versus CO oxidation

Enhanced Thermal Stability and Oxygen Storage Capacity for CexZr1-xO2 (x = 0.4−0.6) Solid Solutions by Hydrothermally Homogenous Doping of Trivalent Rare Earths

Fabrication and Characterization of CeO2-Doped Yttria-Stabilized ZrO2 Composite Particles

Synthesis, thermal stability and catalytic activity of Ce0.72Zr0.18Pr0.1O2-δ nanodispersed solid solution in CO oxidation reaction

Continuous Hydrothermal Flow Synthesis and Characterization of ZrO2 Nanoparticles Doped with CeO2 in Supercritical Water

Investigation of the Physicochemical Properties and Catalytic Activities of Ce0.67M0.33O2(M = Zr4+, Ti4+, Sn4+) Solid Solutions for NO Removal by CO

Research and Industrialization Progress of Ceria-Zirconia Mixed Oxides

Synthesis and Characterization of Nanoscaled Cerium (IV) Oxide Via a Solid‐State Mechanochemical Method

The influence of H2O2 on the properties of CeO2-ZrO2 mixed oxides

Synthesis of Ordered Hexagonal Porous Tin-Doped Zirconium Oxides with a High Surface Area

Controllable synthesis of (Ba0.85Ca0.15)(Zr0.1Ti0.9)O3 submicron sphere by hydroxide co-precipitation method

Zr‐doped CeO2 Hollow slightly‐truncated nano‐octahedrons: One‐pot synthesis, characterization and their application in catalysis of CO oxidation

High Surface Area Ceria Nanoparticles via Hydrothermal Synthesis Experiment Design