Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Characterization of Cerium-Zirconium Solid Solutions Prepared by the Microwave-Assisted Approach

Application of Cerium-Zirconium Solid Solution Prepared by a Microwave-Assisted Method to CO Low-Temperature Oxidation

Synthesis and Characterization of Mesostructured Ceria-Zirconia Solid Solution

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Preparation of Ceria-Zirconia Solid Solution by Urea-Based Hydrothermal-Copricipitation Method and its Catalytic Application

Stability properties and microstructure properties of microwave-sintered CeO2 doped zirconia ceramics

Influence of Ce and Zr precursors on the properties of Ce-Zr solid solution

Preparation of ceria-zirconia solid solution with enhanced oxygen storage capacity and redox performance

Effects of ceria/zirconia ratio on properties of mixed CeO2-ZrO2-Al2O3 compound

Preparation of High Oxygen Storage Capacity and Thermally Stable Ceria–zirconia Solid Solution

Synthesis of Ceria-Zirconia Solid Solutions and their Application in Catalytic Combustion Reaction of CH4 and CO

Catalytic Activity of Ceria-Zirconia Nanostructured Materials Prepared Via Reversed Microemulsion Method

Synthesis and characterization of mesoporous Ce1-xZrxO2 materials by homogeneous coprecipitation

Characterization and Preparation of Ce-Zr-O Solid Solution

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Hydrothermal Crystallization and Characterization of Ce0.5Zr0.5O2 Solid Solution

Study on Ch(4) Conversion over Ce-Zr Solid Solution Supported Nano Pt-Ni Bimetal Catalysts: Preparation and Characterization of Ce-Zr Solid Solution

The Relationship Between Structure and Oxygen Storage Capacity of CexZr1-xO2 Solid Solution

STUDY ON PREPARATION AND OXYGEN STORAGE CAPACITY OF CeO2-ZrO2 SOLID SOLUTION

Enhanced Reduction Properties of Mesostructured Ce0.5Zr0.5O2 Solid Solutions

Characterization and Application of Nanometer Ce_(0.75)Zr_(0.25)O_2 Powder Synthesized by Solid State Chemical Reaction Method