Abstract:Ce1-xZrxO2 (x = 0-0.8) nanoparticulate powders were prepared via a mild urea hydrolysis based hydrothermal method through homogeneous nucleation at 413 K followed by calcination at 773 or 1173 K. X-ray fluorescence (XRF) and energy-dispersive X-ray analysis (EDAX) measurements testify to the good stoichiometric homogeneity of Ce and Zr cations in the as-obtained Ce1-xZrxO2 products. X-ray photoelectron spectroscopy (XPS) and ultraviolet-visible (UV-vis) spectra exhibit that both surface and bulk ratios of Ce3+ to Ce4+ for the as-prepared Ce1-xZrxO2 nanocrystals increased with the zirconium content x. Powder X-ray diffraction (PXRD) patterns and Raman spectra demonstrate that the present Ce1-xZrxO2 samples were single-phase solid solutions with good structural homogeneity and high thermal stability up to 1273 K, and those with x = 0.4-0.6 retained a pseudocubic structure (t" phase) due to the small crystallite size effect. Transmission electron microscopy (TEM) micrographs reveal that the as-prepared CeO2-ZrO2 nanocrystals were highly crystallized with narrow size distribution. Nitrogen adsorption measurements show that the BET specific surface areas of the Ce1-xZrxO2 powders were improved by the incorporation of ZrO2. The PXRD data and high-resolution TEM (HRTEM) images illuminate that the as-prepared and as-calcined Ce1-xZrxO2 (x = 0.4-0.6) powders kept a rather high strain level in the crystal lattice. The lattice strains in our Ce1-xZrxO2 catalysts show a linear relationship with their oxygen storage capacity (OSC) values. This linear correlation is explained on the basis of qualitative structural and defective analysis, and might find use in the screening and design of better-performing three-way catalysts (TWCs). The highest CO-OSC values of the studied CeO2-ZrO2 catalysts appeared for Ce0.5Zr0.5O2 (543 mumol of CO g(-1) at 773 K and 628 mumol of CO g(-1) at 973 K).

Characterization and Preparation of Ce-Zr-O Solid Solution

Effect of Preparation Method on the Surface and Redox Properties of Ce0.67zr0.33o2 Mixed Oxides

Effect of Ce/Zr Atomic Ratio on the TWC Properties of PdO/CexZr1-xO2(x=0-1.0) Catalysts

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Characterization and Preparation of (Ce-Zr)ma1-mo2 Composite Oxides

Investigating the Nano-Scale Structure and Composition Dynamics During the Phase Transition Towards Complete Separation of CeO2-ZrO2 Solid Solution

Dissolution of zirconium–cerium oxide solid solution in an aqueous system

Study on the Properties of Nanometer CeO2 Doped with Zr4+, La3+, Pr3+

Synthesis, thermal stability and catalytic activity of Ce0.72Zr0.18Pr0.1O2-δ nanodispersed solid solution in CO oxidation reaction

Urea-Based Hydrothermally Derived Homogeneous Nanostructured Ce1-Xzrxo2 (X=0-0.8) Solid Solutions: A Strong Correlation Between Oxygen Storage Capacity and Lattice Strain

Enhanced Thermal Stability and Oxygen Storage Capacity for CexZr1-xO2 (x = 0.4−0.6) Solid Solutions by Hydrothermally Homogenous Doping of Trivalent Rare Earths

Preparation and Characterization of Ceria-Zirconia Ceramics Using a Sol-Gel Process

Preparation and characterization of high specific surface area Ce 0.5Zr0.5O2 mixed oxide

Preparation of Zirconia Powders by Sol-gel Process

MOF-Derived CeO2 and CeZrOx Solid Solutions: Exploring Ce Reduction through FTIR and NEXAFS Spectroscopy

General and facile synthesis of ceria-based solid solution nanocrystals and their catalytic properties

Investigation of the Physicochemical Properties and Catalytic Activities of Ce0.67M0.33O2(M = Zr4+, Ti4+, Sn4+) Solid Solutions for NO Removal by CO

Structure and Oxygen Mobility of Ce1-xZrxO2 Prepared by Citric Acid Sol-gel Method

A Structural Study Of The Series Cexzr1-Xo2 Mixed Oxides

Ordered Mesoporous Ce1-xZrxO2 Solid Solutions with Crystalline Walls

The influence of H2O2 on the properties of CeO2-ZrO2 mixed oxides