Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Characterization and Preparation of (Ce-Zr)ma1-mo2 Composite Oxides

Preparation, Characterization, And Thermophysical Properties Of (La0.95sr0.05)(2)Ce2o6.95 Ceramic For Thermal Barrier Coatings

Preparation and Thermal Conductivity of (La0.95Mg0.05)2Ce2O6.95 Ceramics

Effect of Ce/Zr Atomic Ratio on the TWC Properties of PdO/CexZr1-xO2(x=0-1.0) Catalysts

Characterization and Preparation of Ce-Zr-O Solid Solution

Study on the Properties of Nanometer CeO2 Doped with Zr4+, La3+, Pr3+

Structure Properties and OSC Performance of Pr-Ce-Zr Mixed Oxides

Design Structure for Cepr Mixed Oxide Catalysts in Soot Combustion

Effect of Preparation Method on the Surface and Redox Properties of Ce0.67zr0.33o2 Mixed Oxides

Preparation and characterization of high specific surface area Ce 0.5Zr0.5O2 mixed oxide

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Structure and Oxygen Storage Capacity of Pr-doped Ce0.26Zr0.74O2 Mixed Oxides

Study on synthesis and modification of Ti/Ce composite oxide

The capability of CeO2-ZrO2 rare earth complex oxides influenced by different precipitators

Enhanced Thermal Stability and Oxygen Storage Capacity for CexZr1-xO2 (x = 0.4−0.6) Solid Solutions by Hydrothermally Homogenous Doping of Trivalent Rare Earths

Effects of co-precipitation temperature on structure and properties of La and Y doped cerium zirconium mixed oxides

Influence of B-site substituent Ce on thermophysical, oxygen diffusion, and mechanical properties of La2Zr2O7

Influence of (Zn1/3Ta2/3)4+ substitution for Zr4+ in Ce2Zr3(MoO4)9 and the impact on the crystal structure and microwave dielectric properties

Effect of (zn1/3nb2/3)4+ Co-Substitution on the Microwave Dielectric Properties of Ce2Zr3(MoO4)9 Ceramics

Investigation on capability of CeO2-ZrO2 rare earth complex oxides doped by BaO and CaO

Structure Characterization and Monolayer Dispersion Phenomenon of MgO-ZrO2 Prepared by Co-precipitation