Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

The capability of CeO2-ZrO2 rare earth complex oxides influenced by different precipitators

Investigation on capability of CeO2-ZrO2 rare earth complex oxides doped by BaO and CaO

Effect of Preparation Method on the Surface and Redox Properties of Ce0.67zr0.33o2 Mixed Oxides

Structure and Oxygen Storage Capacity of Pr-doped Ce0.26Zr0.74O2 Mixed Oxides

Characterization and Preparation of (Ce-Zr)ma1-mo2 Composite Oxides

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Design Structure for Cepr Mixed Oxide Catalysts in Soot Combustion

Structure Properties and OSC Performance of Pr-Ce-Zr Mixed Oxides

Effects of co-precipitation temperature on structure and properties of La and Y doped cerium zirconium mixed oxides

Study on the Properties of Nanometer CeO2 Doped with Zr4+, La3+, Pr3+

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Enhanced Thermal Stability and Oxygen Storage Capacity for CexZr1-xO2 (x = 0.4−0.6) Solid Solutions by Hydrothermally Homogenous Doping of Trivalent Rare Earths

Modification of CeO2–ZrO2 Mixed Oxides by Coprecipitated/impregnated Sr: Effect on the Microstructure and Oxygen Storage Capacity

Influence of Different Subsistence States of CeO2-ZrO2 Mixed Oxides in Catalyst Coating on Catalytic Properties

Preparation of High-Purityand White CeO_2 by Complex-Precipitation Method and Its Photocatalytic Activit

Modification of Ce0.67Zr0.33O2 mixed oxides by coprecipitated/impregnated Co: Effect on the surface and catalytic behavior of Pd only three-way catalyst

Preparation and characterization of CeO2 with different particle sizes and morphology

The influence of H2O2 on the properties of CeO2-ZrO2 mixed oxides

The Effect of Rare Earth Modification on Ceria–zirconia Solid Solution and Its Application in Pd-only Three-Way Catalyst

Preparation and Characterization of CeO<sub>2</sub> with Different Particle Sizes and Morphology

Effect of Rare-Earth (La, Nd, Pr, Y) Doping on the Properties of X-Y-Ce-Zr-O and X-Y-Z-Ce-Zr-O Nanodispersions for GPF Applications