Investigation on capability of CeO2-ZrO2 rare earth complex oxides doped by BaO and CaO

Zhongjun J. Yan,Jinggang Wang,MingFen Wen,Jing Chen,YongWan Gu

2005-01-01

Rare Metal Materials and Engineering

Abstract:CeO2-ZrO2 rare earth complex oxides doped by BaO and CaO were prepared by coprecipitation. The structure of samples were characterized by X-ray diffractions, and their surface areas and pore structures were measured by BET, and their reductive capacities in low temperature were characterized by H-2-TPR. The results showed that part of BaO or CaO would be integrated with ZrO2 to form BaZrO3 when the content of BaO or CaO was high, which would have an effect on solid solution of rare earth complex oxides. It could increase surface areas Of CeO2-ZrO2 complex oxides in high temperature when loaded a little BaO or CaO. Relative to pure CeO2-ZrO2, it could form more pores after doped by a little BaO or CaO, and the absorption and desorption of gas would benefit from pores, which could accelerate the course of catalytic reaction. But the intrinsic pore structure would be destroyed when the loading of BaO or CaO was high, and the distributing in the area of mesopore was almost disappeared. The porous distributing changed from mesopore to pore. The reductive capacity in low temperature could be highly improved after doped by a little BaO or CaO.