A comparative study of Y 3+ - or/and La 3+ -doped CeO 2 –ZrO 2 -based solid solution
Jiaxiu Guo,Zhonghua Shi,Dongdong Wu,Huaqiang Yin,Yaoqiang Chen
DOI: https://doi.org/10.1557/jmr.2012.435
IF: 2.7
2013-01-01
Journal of Materials Research
Abstract:Ce 0.35 Zr 0.65− x RE x O 2 (RE = Y and La; x = 0 and 0.10) and Ce 0.35 Zr 0.50 Y 0.075 La 0.075 O 2 were prepared by a coprecipitation method. The textures, structures, oxygen storage capacity (OSC), and redox properties of all samples were investigated using Brunauer–Emmett–Teller surface area characterization, x-ray diffraction (XRD), Raman spectra, temperature-programmed technique, and oxygen pulse reaction. The results showed that the fresh Ce 0.35 Zr 0.65 O 2 has cubic phase, 434 μmol/g of OSC, 82 m 2 /g of surface area, and good redox properties; after aging at 1000 °C, Ce 0.35 Zr 0.65 O 2 still has cubic phase, 418 μmol/g of OSC, and 50 m 2 /g of surface area; when Y 3+ or La 3+ is added to CeO 2 –ZrO 2 , the aged Ce 0.35 Zr 0.65− x RE x O 2 (RE = Y and La; x = 0 and 0.10) still remains cubic phase, high OSC, and large surface area (47 m 2 /g); when Y 3+ and La 3+ are simultaneously added into CeO 2 –ZrO 2 , a stable solid solution with cubic phase is formed and has 459 μmol/g of OSC; and the aged Ce 0.35 Zr 0.50 Y 0.075 La 0.075 O 2 reaches to 60 m 2 /g of surface area and has 390 μmol/g of OSC.