Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Effect of Rare-Earth (La, Nd, Pr, Y) Doping on the Properties of X-Y-Ce-Zr-O and X-Y-Z-Ce-Zr-O Nanodispersions for GPF Applications

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Tailoring the Performance of Ni-CaO Dual Function Materials for Integrated CO2 Capture and Conversion by Doping Transition Metal Oxides

Effect of rare earth (La, Nd, Pr, Sm and Y) on the performance of Pd/Ce0.67Zr0.33MO2-δ three-way catalysts

Study of Ag/Cexnd1-Xo2 Nanocubes As Soot Oxidation Catalysts for Gasoline Particulate Filters: Balancing Catalyst Activity and Stability by Nd Doping

The Effect of Rare Earth Modification on Ceria–zirconia Solid Solution and Its Application in Pd-only Three-Way Catalyst

Structure and Oxygen Storage Capacity of Pr-doped Ce0.26Zr0.74O2 Mixed Oxides

Design Structure for Cepr Mixed Oxide Catalysts in Soot Combustion

Impact of dopants on the sulfation, desulfation and NOx reduction performance of Ba-based NOx storage-reduction catalysts

Soot Combustion Performance and H2-TPR Study on Ceria-Based Mixed Oxides

Effect of Rare Earths (la, Pr, Nd, Sm and Y) on the Methane Combustion over Pd/Ce–Zr/Al2O3 Catalysts

Ce‐Pr Mixed Oxide Catalysts with a Fibrous Morphology for Low‐temperature PM Oxidation

Effects of Ni-Doping of Ceria-Based Materials on Their Micro-Structures and Dynamic Oxygen Storage and Release Behaviors

Effects of Fe-doping of Ceria-Based Materials on Their Microstructural and Dynamic Oxygen Storage and Release Properties

New Insight into the Doping Effect of Pr2O3 on the Structure–Activity Relationship of Pd/CeO2–ZrO2 Catalysts by Raman and XRD Rietveld Analysis

The Effect of Nd on the Properties of Ceria–zirconia Solid Solution and the Catalytic Performance of Its Supported Pd-only Three-Way Catalyst for Gasoline Engine Exhaust Reduction

Study on the Properties of Nanometer CeO2 Doped with Zr4+, La3+, Pr3+

The effect of La doping on the structure of Ce0.2Zr0.8O2 and the catalytic performance of its supported Pd-only three-way catalyst

Influence of Rare-Earth Doping Content and Type on Phase Transformation and Transport Properties in Highly Doped CeO2

An Exploration of Soot Oxidation over CeO2-ZrO2 Nanocubes: Do More Surface Oxygen Vacancies Benefit the Reaction?

Application Of Rare Earth Modified Zr-Based Ceria-Zirconia Solid Solution In Three-Way Catalyst For Automotive Emission Control