Abstract:Nanosized copper oxide-zirconia particles containing 10-30 mol% of copper were prepared by using a precipitation technique in aqueous tetramethylammonium hydroxide solutions. Two methods, in situ (INS) and step-by-step (SBS), which differed in the time when the copper salt was introduced to the synthesis procedure, were used, and this allowed a comparison of the properties of the final powders produced using the two modes of preparation. The surface areas and phase compositions were different for the samples prepared from the two different methods after calcination at 500 degreesC. A surface area of 168 m(2) g(-1) was obtained for the sample prepared with the SBS method and 121 m(2) g(-1) for the INS method, both contain 30 mol% copper. Tetragonal ZrO2 was observed from X-ray diffraction patterns for all samples prepared with the SBS method, however, no separate phase of copper or copper oxide was observed. It is proposed that all of the copper is finely distributed on the surface of the ZrO2 particles with the SBS method. For the samples prepared from the INS method, tetragonal ZrO2 was obtained at a low copper content and the peaks indexed to tetragonal ZrO2 shifted to higher angle with the increase of copper content, indicating copper ions being incorporated into the lattice. An amorphous compound was obtained at high copper content (30 mol%). The phase change with the calcination temperature was also investigated for the INS sample containing 30 mol% copper. The studies show that tetragonal ZrO2 and copper oxide were present after calcination at 400 degreesC, and tetragonal ZrO2 with a small amount of monoclinic ZrO2, as well as copper oxide, formed after calcination at 700 degreesC. However, after heating at 500 degreesC, amorphous compounds were obtained, suggesting that 500 degreesC could be a phase transition point. The incorporation of copper in the ZrO2 lattice resulted in a loss of order in the ZrO2 structure when calcined at 500 degreesC, with a further increase in the calcination temperature leading to the phase change.

Structure Characterization and Monolayer Dispersion Phenomenon of MgO-ZrO2 Prepared by Co-precipitation

Preparation and Characterization of Mg-doped ZnO Thin Films by Sol–gel Method

Fabrication and Characterization of Y2O3 Stabilized ZrO2 Films Deposited with Aerosol-Assisted MOCVD

Effect of Solution Concentrations on Crystal Structure, Surface Topographies and Photoluminescence Properties of ZnO Thin Films

Coprecipitation Synthesis of MgO-Doped ZrO<sub>2</sub> Nano Powder

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Effect of MgO/ZnO ratio on the formation process of MgxZn1-xO ceramics

Facile Synthesis and Characterization of ZrO₂ Nanoparticles via Modified Co-Precipitation Method

Synthesis of Mg and Zn diolates and their use in metal oxide deposition

Preparation and characterization of CuO–ZrO2 nanopowders

Investigation on the Preparation and Properties of Monodispersed Al2O3ZrO2 Nanopowder Via Co-precipitation Method

Preparation and characterization of nano-scale Y2O3-ZrO2 powder by heterogeneous precipitation

Characterization and Preparation of (Ce-Zr)ma1-mo2 Composite Oxides

Preparation and Microstructures of CoAl(2)O(4) ZrO(2) Composite

Structure Characterization Of Wo3/Zro2 Catalysts By Raman Spectroscopy

Deposition of Sol-Gel ZnO:Mg Films and Investigation of Their Structural and Optical Properties

Initial Oxidation and Interfacial Diffusion of Zn on Faceted MgO(111) Films.

Synthesis of Mg X Zn 1- X O under High Pressure and High Temperature

Preparation of Magnesium Stabilized Zirconia Nanoparticles by Buffer Solution Precipitation

Fabrication, characterization, and acid solubility of MgO-Nd2Zr2O7 composite ceramics for inert matrix fuel

Preparation and characterization of lamellar-like Mg(OH)2 nanostructures via natural oxidation of Mg metal in formamide/water mixture