Abstract:The results of experimental investigations using laser speckle interferometry on small size three-point bending notched beams and using photoelastic coating and the strain gauges on very large size compact tension specimens of concrete are presented in detail. The investigations showed that there exists a stage of stable crack propagation before unstable fracture occurs. The results are in agreement with other researchers' investigations using moire interferometry, holographic interferometry, dye-impregnation method and microscope. Further detailed study shows that the three different states, i.e., crack initiation, stable crack propagation and unstable fracture can be distinguished in the fracture process in concrete structures. In order to predict the crack propagation during the fracture process in quasi-brittle materials a double-K criterion is proposed. The double-K criterion consists of two size-independent parameters. Both of them are expressed in terms of the stress intensity factors. One of them reflects the initial cracking toughness, denoted with K ini , which can be directly evaluated by the initial cracking load, P ini , and the precast crack length, a 0 , using a formula of LEFM. The other one refers to the unstable fracture toughness, denoted with K un , which can be obtained inserting the maximum load, P max , and the effective crack length, a, into the same formula of LEFM. The values of the two parameters, K Ic ini and K Ic un , obtained from the small size three-point bending notched beams and the large size compact tension specimens show that K Ic ini and K Ic un are size-independent. Evaluating with the K-resistance curves obtained from the same test data, it is found that the proposed double-K criterion is equivalent to it in basic principle, but, the double-K criterion can be applied more easily than the K-resistance curve. Finally, as a practical example, the application of the double-K criterion to the prediction of the crack propagation in a concrete dam is discussed.

Experimental Evaluation of Fracture Toughness for Epoxy-Repaired Concrete Considering Crack Deflection Angle

Experimental Investigation On Mode Ii Fracture Toughness K-Iic Of Concrete And Fracture Behavior

Experimental Investigation on Mode II Fracture Toughness K<sub>IIC</sub> of Concrete and Fracture Behavior

Experimental study on fracture toughness K_(Ⅱc) of concrete

New concrete cracking model established based on fracture mechanics and damage theory

Experimental study on fracture properties of self-compacting concrete

Experimental Study on Some Factors Affecting Fracture Property of Concrete

Fracture Toughness And Microstructure Of Concrete At Early-Ages

Experimental measurement of double-K fracture parameters of concrete with small-size aggregates

Numerical Simulation of Fracture and Damage Behaviour of Concrete at Different Ages

Fracture Toughness of Ordinary Plain Concrete Under Three-Point Bending Based on Double-K and Boundary Effect Fracture Models

Effect of Size and Cohesive Assumptions on the Double-K Fracture Parameters of Concrete

Determination of double-Determination of double- K criterion for crack propagation in quasi-brittle fracture Part I: experimental investigation of crack propagation

Dynamic Fracture Catastrophe Model of Concrete Beam under Static Load

Fracturing behaviors of FRP-strengthened concrete structures

A Fracture toughness criterion for concrete

DETERMINATION OF CRACK INITIATION AND EQUIVALENT CRACK LENGTH OF LOW STRENGTH CONCRETE USING STRAIN GAUGES

A comparative study on five approaches to evaluate double-K fracture toughness parameters of concrete and size effect analysis

Quantitative characterization and mechanism analysis on thickness-dependent size effect of concrete fracture

Determination of Fracture Properties of Concrete Using Size and Boundary Effect Models