Abstract:Fracture tests are a necessary means to obtain the fracture properties of concrete, which are crucial material parameters for the fracture analysis of concrete structures. This study aims to fill the gap of insufficient test results on the fracture toughness of widely used ordinary C40~C60 concrete. A three-point bending fracture test was conducted on 28 plain concrete and 6 reinforced concrete single-edge notched beam specimens with various depths of prefabricated notches. The results are reported, including the failure pattern, crack initiation load, peak load, and complete load versus crack mouth opening displacement curves. The cracking load showed significant variation due to differences in notch prefabrication and aggregate distribution, while the peak load decreased nonlinearly with an increase in the notch-to-height ratio. The reinforced concrete beams showed a significantly higher peak load than the plain concrete beams, attributed to the restraint of steel reinforcement, but the measured cracking load was comparable. A compliance versus notch-to-height ratio curve was derived for future applications, such as estimating crack length in crack growth rate tests. Finally, fracture toughness was determined based on the double-K fracture model and the boundary effect model. The average fracture toughness value for C50 concrete from this study was 2.0 , slightly smaller than that of lower-strength concrete, indicating the strength and ductility dependency of concrete fracture toughness. The fracture toughness calculated from the two models is consistent, and both methods employ a closed-form solution and are practical to use. The derived fracture toughness was insensitive to the discrete parameters in the boundary effect model. The insights gained from this study significantly contribute to our understanding of the fracture toughness properties of ordinary structural concrete, highlighting its potential to shape future studies and applications in the field.

Fracture Toughness And Microstructure Of Concrete At Early-Ages

Stochastic Fracture of Concrete Composites: A Mesoscale Methodology

Experimental Study on Some Factors Affecting Fracture Property of Concrete

Influence of Mineral Admixture on Early-Age Concrete Cracking

Early Age Properties and Cracking Control of Concrete

Experimental study on fracture properties of self-compacting concrete

Experimental Study on the Fracture Toughness of Concrete under Different Curing Conditions

Experimental investigation on the effect of coarse aggregate size and silica fume dosage to the fracture parameters of concrete

Fracture Property Investigation of Young Concrete Using TPM

Interpretation of Microstructure Development of Early-Age Concrete by Electrical Resistivity Measurement

Fracture Property of Steel Fiber Reinforced Concrete at Early Age

Numerical Simulation of Fracture and Damage Behaviour of Concrete at Different Ages

Correlation of Mechanical and Microstructure Development of Early-Age Concrete by Electrical Resistivity Measurement

Experimental studies on the thermal fracture toughness of concrete and mortar in early ages

THEORETICAL INVESTIGATION TO CRACKING PREDICTION OF EARLY-AGE CONCRETE

Study on Relation Between Early-age Performance of Concrete and Its Durability

Fracture Toughness of Ordinary Plain Concrete Under Three-Point Bending Based on Double-K and Boundary Effect Fracture Models

New concrete cracking model established based on fracture mechanics and damage theory

Evaluation of Concrete Material Properties at Early Age

Study on Performance of High Strength Concrete at Early Age

Age-dependent Size Effect and Fracture Characteristics of Ultra High Performance Concrete