Abstract:In order to shorten construction periods, concrete is often cured using steam and is loaded at an early age. This changes the performance and even the durability of the concrete compared to concrete that has been cured under normal conditions. Thus, the pattern and the mechanism of concrete performance change under different curing conditions, and loading ages are of great significance. The development of brittleness under different curing conditions and loading ages was studied. The evaluation methods that were used to determine concrete brittleness were expounded. Steam, standard, and natural curing conditions were carried out on single-side notched concrete beams as well as on a concrete prism and cubic blocks. The compressive strength and splitting tensile strength of the concrete blocks along with the fracture performance of the concrete beams were tested after 3, 7, 28, and 90 days. The steam curing condition significantly improved the strength of concrete before 28 days had passed, and the standard curing condition improved the strength of concrete after 28 days. Based on the experimental fracture parameters, a two-parameter fracture model was applied to study the development of fracture toughness KICS, critical crack tip opening displacement CTODc, and critical strain energy release rate GICS with hydration age under different curing conditions. With respect to long-term performance, the standard curing condition was better at resisting concrete crack propagations than the steam curing condition was. The characteristic length lch and the material length Q under the three curing conditions and the long-term development of brittleness in the concrete indicated that steam curing increased the concrete brittleness. Considering the effects of the curing condition and the loading age, a time-dependent concrete fracture toughness model was established, and the predicted value of the model was verified against the measured value. The results indicated that the model was able to accurately predict the fracture toughness with an error rate of less than 16%.

Fracture Property Investigation of Young Concrete Using TPM

Fracture Toughness And Microstructure Of Concrete At Early-Ages

Experimental study on fracture properties of self-compacting concrete

Experimental Study on Some Factors Affecting Fracture Property of Concrete

Fracture Property of Steel Fiber Reinforced Concrete at Early Age

Experimental Study on the Fracture Toughness of Concrete under Different Curing Conditions

Numerical Simulation of Fracture and Damage Behaviour of Concrete at Different Ages

Concrete Thermal Cracking Analysis with Cement Hydration Model and Equivalent Age Method

Influence of Mineral Admixture on Early-Age Concrete Cracking

Early Age Properties and Cracking Control of Concrete

Numerical simulation of cracking of early-age concrete three-point beams

New concrete cracking model established based on fracture mechanics and damage theory

Fracture Toughness of Ordinary Plain Concrete Under Three-Point Bending Based on Double-K and Boundary Effect Fracture Models

THEORETICAL INVESTIGATION TO CRACKING PREDICTION OF EARLY-AGE CONCRETE

Research on Fracture Characteristic of Fly Ash Concrete Based on Dual-G Criterion

The Test and Calculation of Fracture Resistance Property for Steel Fiber-Reinforced Concrete in Early Age

Experimental investigation on the effect of coarse aggregate size and silica fume dosage to the fracture parameters of concrete

Relationship Between Characteristic Tensile Strain and Curing Age of Concrete

Brittleness of Concrete under Different Curing Conditions

Numerical Analysis of Softening Relationship for Early-Age Concrete

Experimental studies on the thermal fracture toughness of concrete and mortar in early ages