Abstract:Double-G fracture model, a new analytical model describing fracture behaviour on cracked concrete, was recently proposed by Xu and Zhao based on the conception of energy release rate. This model couples the Griffith brittle fracture theory with the bridging softening property of concrete, and it is an extension of double-K fracture model proposed by Xu and Reinhardt. In this model, two fracture parameters, i.e., the initiation fracture energy release GIcini and the unstable fracture energy release GIcun, are termed to distinguish the different crack propagation stages undergoing during the whole fracture process in concrete. The difference between the two parameters, written as GIcc, is assumed to come from the contribution by aggregate bridging interlock, which results in the presence of fracture process zone. In our present work, firstly, the new model is elaborately introduced. Then, fracture tests are conducted, where besides three-point bending beams, a new testing method, called wedge-splitting on compact tension is adopted. In the experiments, electrical strain gauges are used to measure initial cracking load. Based on recorded load–crack mouth opening displacement curve (P–CMOD) or load–displacement curve (P–δ) and load–strain curve (P–ε), double-G fracture parameters are experimentally determined. Further more, based on the assumed three parameters relationship among GIcini, GIcun and GIcc, unstable fracture energy release are calculated. A comparable result between the measured GIcun-e and the calculated GIcun-c confirms this assumption. In order to verify the feasibility of this new model, the effective double-K fracture parameters converted by double-G fracture parameters using K=EG are compared with the double-K fracture parameters calculated by double-K fracture model. It is found that there is a good agreement. Another two series of different initial crack-depth ratios three-point bending beams carried out by Refai and Swartz are also collected to provide more experimental verification. It shows that the results obtained from the double-G fracture model agree well with those of double-K fracture model.

DETERMINATION OF CRACK INITIATION AND EQUIVALENT CRACK LENGTH OF LOW STRENGTH CONCRETE USING STRAIN GAUGES

Shear Tests of Reinforced Concrete Beams with the Influence of Initial Shear Cracks

Determination of double-Determination of double- K criterion for crack propagation in quasi-brittle fracture Part I: experimental investigation of crack propagation

Numerical simulation of cracking of early-age concrete three-point beams

Experimental measurement of double-K fracture parameters of concrete with small-size aggregates

Determination of double- K criterion for crack propagation in quasi-brittle fracture, Part II: Analytical evaluating and practical measuring methods for three-point bending notched beams

Determination of Concrete Fracture Parameters from a Three-Point Bending Test

Influence of Mineral Admixture on Early-Age Concrete Cracking

Determination of fracture parameters for crack propagation in concrete using an energy approach

Experimental study on fracture properties of self-compacting concrete

Experimental determination of fracture parameters for crack propagation in hardening cement paste and mortar

Determination of Double-K Fracture Parameters Using Semi-Circular Bend Test Specimens

Determination of double-K criterion for crack propagation in quasi-brittle fracture, Part III: Compact tension specimens and wedge splitting specimens

Fracture Toughness of Ordinary Plain Concrete Under Three-Point Bending Based on Double-K and Boundary Effect Fracture Models

The Influence of Span/Depth Ratio on the Double-K Fracture Parameters of Concrete

Experimental investigation and modified calculation model of critical crack propagation length of concrete

EXPRIMENTS FOR DETERMING THE DOUBLE-K FRACTURE PARAMETERS OF CONCRETE OF THE THREE GORGES DAM

The theoretical basis of testing methods to determine double-K criterion for crack propagation in concrete: technical report of the RILEM TC265-TDK

Quantitative characterization and mechanism analysis on thickness-dependent size effect of concrete fracture