Failure Analysis on Unexpected Fracture of the Hydraulic Expansion Mandrel for Tube to Tubesheet Expanding in the Steam Generator of Nuclear Power Plant
Guang-Qing He,Xiao-Lei Yang,Yi Gong,Dong-Qing Lu,Jian-Guo Deng,Jia-Lei Gu,Qiong Wu,Zhen-Guo Yang
DOI: https://doi.org/10.1016/j.engfailanal.2023.107062
IF: 4
2023-01-01
Engineering Failure Analysis
Abstract:Hydraulic expansion is commonly adopted for the tube to tubesheet expansion in the steam generator of nuclear power plants, and its quality greatly influences the stable and reliable operation of the steam generator. In this paper, an unexpected fracture of the hydraulic expansion mandrel occurred during the hydraulic expansion process, which caused the internal bulge defect (IBD) in the expanding area of the heat exchange tube. The corrosion test results showed that the IBD area had higher susceptibility to stress corrosion cracking (SCC) than the original tubes, which might lead to premature failure of the heat exchange tube in practical operation. To find out the root causes of this failure, the fracture morphologies of the hydraulic expansion mandrel were observed under the optical microscope (OM) and the scanning electron microscope (SEM), and the stress distribution during service were analyzed by mechanical calculation, The results indicated that the hydraulic expansion mandrel was repeatedly loaded by high-pressure medium during service, thus its weakest point was fractured due to high strain level and low cyclic number inelastic strain fatigue. Based on the results, the underlying mechanisms were discussed, and the countermeasures were proposed. The achievements of this paper provide theoretical and practical support for preventing similar failure and ensuring the expansion quality of the steam generator tubes for nuclear power plants.