Abstract:Polyimide (PI) films have excellent comprehensive properties and bright prospects in the next generation of optoelectronic and microelectronic applications. PIs were synthesized by aromatic diamines and alicyclic dianhydrides considered to be the most effective method for preparing polyimides with high light transmittance and low dielectric constant. In order to improve the overall performance of polyimide, the introduction of a large trifluoromethyl group into the main chain is also considered a powerful strategy. In this article a novel diamine containing 6 trifluoromethyl groups has been designed and synthesized by Suzuki reaction. Afterwards, PIs were synthesized with fluorinated aromatic dianhydride and alicyclic dianhydride through a two-step method. The two PIs have excellent solubility: PI-a and PI-b exhibited excellent solubility in common polar solvents. Such as DMF, DMAc, NMP and DMSO at room temperature, and PI-a was soluble in low-boiling solvents such as ethyl acetate, CH2Cl2 and CHCl3 at room temperature. PI-b was soluble in low-boiling solvents acetone and CHCl3 at room temperature, which was rarely seen in other aromatic polyimides. Soluble in common organic solvents, especially low boiling point solvents, made these polymers easy to process and suitable for processing technology in solution. This was an important modification for PIs. They also showed good high temperature resistance: the decomposition temperature (T5%) of two PIs were 520 °C and 475 °C. In addition, the residual rate at 790 °C was 50 % and 49 % respectively. Two PI films had a very low dielectric constant 2.26 and 2.24, respectively, which was attributed to the hyperbranched structure and strong electron-withdrawing fluorine-containing groups. PI-a and PI-b also had low water absorption of 0.66 % and 0.72 %, respectively. The transmittance of PI-a and PI-b high transparent films at 450 nm were 74% and 82%, respectively. The significant optical modification was mainly due to the weak electron-accepting alicyclic unit and the large trifluoromethyl electron withdrawing group. This work mainly provided an effective strategy for synthesizing comprehensive excellent performance PIs with high transmittance, excellent solubility, low water absorption, high heat resistance and low dielectric constant.

Achieving Both Low Thermal Expansion and Low Birefringence for Polyimides by Regulating Chain Structures

A comprehensive study on the effect of molecular chain flexibility on the low-temperature curing ability of polyimides

Near-Zero Thermal Expansion and High Heat-Resistance Polyimide Films Based on a Symmetric and Rigid Pyrazine Structure

Tunable Permittivity in High-Performance Hyperbranched Polyimide Films by Adjusting Backbone Rigidity

Increasing Twist Rigidity to Prepare Polyimides with Low Dielectric Constants and Dissipation Factors over a Wide Temperature Range

Preparation and characterization of organic soluble polyimides with low dielectric constant containing trifluoromethyl for optoelectronic application

Synergistic Enhancement of Mechanical and Dielectric Properties in Transparent Polyimides by Regulating Hydrogen Bonding and Microbranched Cross-Linking Structure

Synthesis of Colorless Polyimides with High T G and Low Coefficient of Thermal Expansion from Benzimidazole Diamine Containing Biamide

Based on Rigid Xanthone Group and Hydrogen Bonding to Construct Polyimide Films with Low Coefficient of Thermal Expansion, High Temperature Resistance, and Fluorescent Property

Novel semi-N-methyl substituted bisbenzimidazole based polyimide films with low coefficient of thermal expansion and high Tg

Multifunctional Polyimides by Direct Silyl Ether Reaction of Pendant Hydroxy Groups: Toward Low Dielectric Constant, High Optical Transparency and Fluorescence

Synthesis of soluble polyimides for vertical alignment of liquid crystal via one-step method

Reduced Coefficients of Linear Thermal Expansion of Colorless and Transparent Semi-Alicyclic Polyimide Films Via Incorporation of Rigid-Rod Amide Moiety: Preparation and Properties

Incorporating bis-benzimidazole into polyimide chains for effectively improving thermal resistance and dimensional stability

High Performance Transparent Polyimides by Controlling Steric Hindrance of Methyl Side Groups

Low temperature curing polyimides with covalent-boned 5-aminobenzimidazole

Improving dimensional stability at high temperature and toughness of polyimide films via adjustable entanglement density

Preparation and properties of polyimides containing cyano and Cardo structures

Structure‐Property Relationship of Polyimide Fibers with High Tensile Strength and Low Dielectric Constant by Introducing Benzimidazole and Trifluoromethyl Units

High Refractive Index Polyimides Derived from 2,7-Bis(4-aminophenylenesulfanyl)thianthrene and Aromatic Dianhydrides

High-Frequency 5g Substrate: Low Dielectric Biphenyl Polyimide with Low Cte and High Thermal Stability