Abstract:A colorless and high temperature resistant fluorinated polyimide (PI) film based on a novel cross‐linkable diamine monomer 4,4′‐diamino‐4″‐(2,3,5,6‐tetrafluoro‐4‐ethylenephenoxy) triphenylmethane (DFPTM) was successfully prepared. The special triphenylmethane backbone and the bulky tetrafluorostyrol pendant group in DFPTM gave the PI material eximious solubility in organic solvents, high tensile properties, good thermal stability, and excellent optical transparency (cutoff wavelength for 331 nm and light transmittance above 94% at 450 nm). Furthermore, the styryl could initiate self‐crosslinking reaction to form a dense three‐dimensional network structure by thermal curing. Hence, the cross‐linked PI film showed superior combination property (including excellent resistance to solvents). It's Tg increased by 57.1–306.0°C, the 5% thermal weight‐loss temperature improved by 10.2% to 500.0°C, and the tensile strength enhanced by 17.5% to 39.7 MPa. Moreover, after thermal curing, the cross‐linked PI attained a lower elongation at break from 8.1 to 3.9%, and the thermal expansion coefficient reduced from 82.2 to 68.8 ppm/°C without obvious loss of optical transparency (cutoff wavelength for 347 nm and light transmittance remained 93.0% at 450 nm). An organosoluble and cross‐linkable polyimide (PI) film material derived from a novel diamine 4,4'‐diamino‐4″‐(2,3,5,6‐tetrafluoro‐4‐ethylenephenoxy) triphenylmethane (DFPTM) is successfully prepared. It is demonstrated that the obtained cross‐linked PI by curing at 260°C for 2 hr under vacuum exhibits superior balanced optical transparency and high‐temperature stability with transmittance for 93.0% at 450 nm, Tg to 306.0°C as well as T5% up to 500.0°C.

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is how to synthesize a colorless, high - temperature - resistant polyimide (PI) material with both high optical transparency and excellent thermal stability through reasonable molecular design. Specifically, the researchers face the following key challenges: 1. **Balance between optical transparency and thermal stability**: Traditional PI materials have strong absorption from ultraviolet to visible light due to the formation of intermolecular and intramolecular charge - transfer complexes (CTC), presenting a dark brown color, which limits their applications in the optoelectronic field. In order to improve optical transparency, methods such as introducing alicyclic structures, fluorine atoms, and bulky substituents are usually adopted, but these methods often damage the thermal properties of the materials to a certain extent. 2. **Balance between solvent processability and solvent resistance**: In the manufacturing process of multi - layer optoelectronic devices, polymer materials need to have good resistance to organic solvents. This means that the initial material should be soluble in organic solvents, but should be insoluble after film formation. Introducing cross - linkable side groups is an effective strategy, which can improve the solvent resistance and other properties of the materials while maintaining processability. 3. **Comprehensive performance improvement of high - performance PI materials**: By introducing specific chemical structures (such as triphenylmethane skeletons and tetrafluorostyrene side groups), the researchers hope that the synthesized PI materials can not only have high optical transparency and excellent thermal stability, but also have good mechanical properties, dimensional stability, and chemical solvent resistance. For this purpose, the author designed and synthesized a diamine monomer 4,4' - diamino - 4'' - (2,3,5,6 - tetrafluoro - 4 - vinylphenoxy)triphenylmethane (DFPTM) containing a new cross - linkable bulky tetrafluorostyrene side group and an organic - solvent - soluble triphenylmethane skeleton structure. This design aims to overcome the contradiction between optical transparency and thermal stability in traditional PI materials and provide high - performance PI materials for flexible wearable display technologies. ### Main solutions - **Molecular design**: Introduce tetrafluorostyrene side groups and triphenylmethane skeleton structures to improve the optical transparency, thermal stability, and solvent solubility of the materials. - **Synthesis method**: Prepare the target PI materials by a two - step chemical imidization reaction using DFPTM and commercial aromatic dianhydride 6FDA. - **Performance test**: Conduct a comprehensive characterization of the solubility, thermal stability, optical properties, and mechanical properties of the synthesized PI materials to verify whether they have achieved the expected design goals. Through the above methods, the researchers successfully synthesized a PI material with both high optical transparency (cut - off wavelength of 331 nm and light transmittance of more than 94% at 450 nm) and excellent thermal stability (glass transition temperature Tg increased to 306 °C and 5% thermal weight loss temperature increased to 500 °C). In addition, the cross - linked PI film also shows a lower elongation at break and a thermal expansion coefficient, and maintains a high optical transparency.

Synthesis and properties of novel colorless and thermostable polyimides containing cross‐linkable bulky tetrafluorostyrol pendant group and organosoluble triphenylmethane backbone structure

Synthesis and Characterization of Organo-Soluble Polyimides Based on Polycondensation Chemistry of Fluorene-Containing Dianhydride and Amide-Bridged Diamines with Good Optical Transparency and Glass Transition Temperatures over 400 °C

Synthesis of Highly Transparent and Thermally Stable Copolyimide with Fluorine‐containing Dianhydride and Alicyclic Dianhydride

Synthesis and properties of fluorinated polyimides from 1,1-bis(4-amino-3,5-dimethylphenyl)-1-(3,4,5-trifluorophenyl)-2,2,2-trifluoroethane and various aromatic dianhydrides

Synthesis and Properties of Optically Transparent Fluoro-Containing Polyimide Films with Reduced Linear Coefficients of Thermal Expansion from Organo-Soluble Resins Derived from Aromatic Diamine with Benzanilide Units

Synthesis and Properties of Cost-Effective Light-Color and Highly Transparent Polyimide Films from Fluorine-Containing Tetralin Dianhydride and Aromatic Diamines

Synthesis and properties of polyimides from a diamine containing side diphenylphosphine oxide and trifluoromethyl groups

Solubility, electrochemical behavior and thermal stability of polyimides synthesized from 1,3,5-triazine-based diamine

Preparation and Properties of Pale‐colored and Optically Transparent Fluoro‐containing Polyimide Films with Low Solar Absorptivity and Enhanced High‐temperature Dimensional Stability for Potential Applications in Space Environments

Soluble and Transparent Polyimides with High Tg from a New Diamine Containing Tert‐butyl and Fluorene Units

Novel Polyfluorinated Polyimides Derived from Α,α-Bis(4-amino-3,5-difluorophenyl)phenylmethane and Aromatic Dianhydrides: Synthesis and Characterization

Synthesis and Properties of Ultralow Dielectric Constant Porous Polyimide Films Containing Trifluoromethyl Groups

Preparation and characterization of organic soluble polyimides with low dielectric constant containing trifluoromethyl for optoelectronic application

Synthesis of highly transparent and heat-resistant polyimides containing bulky pendant moieties: Synthesis of highly transparent and heat-resistant polyimides containing bulky pendant moieties

Multifunctional Polyimides by Direct Silyl Ether Reaction of Pendant Hydroxy Groups: Toward Low Dielectric Constant, High Optical Transparency and Fluorescence

Preparation and Characterization of Light-Colored Polyimide Nanocomposite Films Derived from a Fluoro-Containing Semi-Alicyclic Polyimide Matrix and Colloidal Silica with Enhanced High-Temperature Dimensionally Stability

Synthesis and properties of modified thermoplastic polyimide films with good dielectric properties at high frequency and enhanced thermal stability via incorporation of rigid ester and biphenyl structural units

Soluble and Cross-Linkable Polyimides from a Vanillin-Derived Diamine: Preparation, Post-Polymerization and Properties

Synthesis And Properties Of Cross-Linkable High Molecular Weight Fluorinated Copolyimides

Synthesis and Characterization of Novel Fluorinated Polyimides Derived from 4-Phenyl-2,6-bis[4-(4′-amino-2′-trifluoromethyl-phenoxy)phenyl]pyridine and Dianhydrides

Synthesis and Characterization of Thioether-Containing Polyimides with High Refractive Indices