Abstract:Polyimide (PI) films have excellent comprehensive properties and bright prospects in the next generation of optoelectronic and microelectronic applications. PIs were synthesized by aromatic diamines and alicyclic dianhydrides considered to be the most effective method for preparing polyimides with high light transmittance and low dielectric constant. In order to improve the overall performance of polyimide, the introduction of a large trifluoromethyl group into the main chain is also considered a powerful strategy. In this article a novel diamine containing 6 trifluoromethyl groups has been designed and synthesized by Suzuki reaction. Afterwards, PIs were synthesized with fluorinated aromatic dianhydride and alicyclic dianhydride through a two-step method. The two PIs have excellent solubility: PI-a and PI-b exhibited excellent solubility in common polar solvents. Such as DMF, DMAc, NMP and DMSO at room temperature, and PI-a was soluble in low-boiling solvents such as ethyl acetate, CH2Cl2 and CHCl3 at room temperature. PI-b was soluble in low-boiling solvents acetone and CHCl3 at room temperature, which was rarely seen in other aromatic polyimides. Soluble in common organic solvents, especially low boiling point solvents, made these polymers easy to process and suitable for processing technology in solution. This was an important modification for PIs. They also showed good high temperature resistance: the decomposition temperature (T5%) of two PIs were 520 °C and 475 °C. In addition, the residual rate at 790 °C was 50 % and 49 % respectively. Two PI films had a very low dielectric constant 2.26 and 2.24, respectively, which was attributed to the hyperbranched structure and strong electron-withdrawing fluorine-containing groups. PI-a and PI-b also had low water absorption of 0.66 % and 0.72 %, respectively. The transmittance of PI-a and PI-b high transparent films at 450 nm were 74% and 82%, respectively. The significant optical modification was mainly due to the weak electron-accepting alicyclic unit and the large trifluoromethyl electron withdrawing group. This work mainly provided an effective strategy for synthesizing comprehensive excellent performance PIs with high transmittance, excellent solubility, low water absorption, high heat resistance and low dielectric constant.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop polyimide (PI) with high light transmittance, easy processability, low dielectric constant, high heat resistance and low water absorption rate to meet the requirements in the fields of advanced optoelectronics and microelectronics. Specifically, the author improves the comprehensive properties of polyimide, especially its solubility, optical transparency and dielectric properties, by introducing trifluoromethyl (-CF₃) and alicyclic structures. ### Main problems of the paper 1. **Improving the solubility of polyimide**: Traditional fully aromatic polyimides are insoluble, difficult to process and have a relatively dark color due to the rigid - chain interactions and highly conjugated molecular chains that are prone to form charge - transfer complexes (CTC). Therefore, it is necessary to improve the solubility of polyimide to make it easy to process. 2. **Reducing the dielectric constant**: In order to meet the requirements of high - speed communication (such as 5G) and microelectronic integrated circuits, polyimide materials need to have a lower dielectric constant to reduce losses in signal transmission. 3. **Increasing optical transparency**: In optoelectronic applications, polyimide needs to have high optical transparency, especially in the visible light range. 4. **Improving heat resistance and reducing water absorption rate**: Polyimide materials need to remain stable in a high - temperature environment and have a low water absorption rate in a humid environment to ensure that their properties are not affected. ### Solutions The author solves the above problems through the following strategies: 1. **Designed and synthesized a new diamine monomer containing six trifluoromethyl groups**: A new type of diamine monomer was synthesized through the Suzuki reaction. This monomer contains multiple trifluoromethyl groups to increase the flexibility of the molecular chain and reduce the intermolecular forces, thereby improving solubility and dielectric constant. 2. **Synthesized polyimide by a two - step method**: Fluorinated aromatic dianhydride (6FDA) and alicyclic dianhydride (CBDA) were polymerized with the newly designed diamine monomer, and finally dehydrated at a high temperature to generate organically soluble hyperbranched polyimides (PI - a and PI - b). 3. **Introduced trifluoromethyl and alicyclic structures**: These structures not only improve the optical transparency of polyimide, but also reduce the dielectric constant and water absorption rate. ### Experimental results - **Solubility**: PI - a and PI - b show excellent solubility in common polar solvents (such as DMF, DMAc, NMP and DMSO), and also have good solubility especially in low - boiling - point solvents (such as ethyl acetate, CH₂Cl₂ and CHCl₃). - **Dielectric constant**: The dielectric constants of PI - a and PI - b are 2.26 and 2.24 (1 MHz) respectively, which are attributed to the strongly electron - withdrawing trifluoromethyl and alicyclic structures. - **Optical transparency**: The light transmittances of PI - a and PI - b at 450 nm are 74% and 82% respectively, which are significantly better than those of traditional fully aromatic polyimides. - **Heat resistance**: The decomposition temperatures (T₅%) of PI - a and PI - b are 520°C and 475°C respectively, and the residual rates at 790°C are 50% and 49% respectively. - **Water absorption rate**: The water absorption rates of PI - a and PI - b are 0.66% and 0.72% respectively, showing low water absorption. ### Conclusion This research provides an effective strategy to synthesize polyimide materials with high light transmittance, excellent solubility, low water absorption rate, high heat resistance and low dielectric constant by introducing trifluoromethyl and alicyclic structures. These polyimide films with excellent properties are expected to be used as flexible transparent substrates or insulating layer materials for integrated circuit devices.

Preparation and characterization of organic soluble polyimides with low dielectric constant containing trifluoromethyl for optoelectronic application

Organosoluble polyimides with low dielectric constant prepared from an asymmetric diamine containing bulky m-trifluoromethyl phenyl group

Synthesis and properties of polyimides from a diamine containing side diphenylphosphine oxide and trifluoromethyl groups

Synthesis and Characterization of Novel Fluorinated Polyimides Derived from 4-Phenyl-2,6-bis[4-(4′-amino-2′-trifluoromethyl-phenoxy)phenyl]pyridine and Dianhydrides

Synthesis and properties of novel colorless and thermostable polyimides containing cross‐linkable bulky tetrafluorostyrol pendant group and organosoluble triphenylmethane backbone structure

Preparation of fluorinated poly(benzoxazole-co-imide) with low dielectric constants based on the thermal rearrangement reaction of o-hydroxy polyimides

Synthesis and Characterization of High Fluorine‐containing Polyimides with Low‐dielectric Constant

High Optical Transparency, Low Dielectric Constant and Light Color of Organosoluble Fluorinated Polyimides Based on 10,10-Bis[4-(4-amino-3-trifluoromethylphenoxy)phenyl]-9(10h)-anthrone

Synthesis and Properties of Optically Transparent Fluoro-Containing Polyimide Films with Reduced Linear Coefficients of Thermal Expansion from Organo-Soluble Resins Derived from Aromatic Diamine with Benzanilide Units

Construction of fluorenyl‐modified low dielectric constant polyimide films with excellent mechanical properties and optical transparency

Synthesis and Characterization of Organo-Soluble Polyimides Based on Polycondensation Chemistry of Fluorene-Containing Dianhydride and Amide-Bridged Diamines with Good Optical Transparency and Glass Transition Temperatures over 400 °C

Polyimide resins with superior thermal stability, dielectric properties, and solubility obtained by introducing trifluoromethyl and diphenylpyridine with different bulk pendant groups

Enhanced performance of low-dielectric siloxane-polyimide copolymers: Synthesis and properties

Soluble and Cross-Linkable Polyimides from a Vanillin-Derived Diamine: Preparation, Post-Polymerization and Properties

Preparation and Properties of Low-Dielectric Polyimide Films Containing Tert-Butyl

Preparation of fluorinated polyimides with low dielectric constants and low dielectric losses by combining ester groups and triphenyl pyridine structures

Fluorinated polyimide with triphenyl pyridine structure for 5G communications: Low dielectric, highly hydrophobic, and highly transparent

Transparent and highly organosoluble aromatic polyimides with twisted backbone and bulky side substituents for flexible substrate materials

Preparation of Triphenylamine Polyimides with Low Dielectric Constants with Different Side Group Sizes Based on Β-Relaxation Theory

Polyimide Films Based on β-Cyclodextrin Polyrotaxane with Low Dielectric and Excellent Comprehensive Performance

Preparation and Properties of Pale‐colored and Optically Transparent Fluoro‐containing Polyimide Films with Low Solar Absorptivity and Enhanced High‐temperature Dimensional Stability for Potential Applications in Space Environments