Abstract:Bifacial passivated emitter and rear cells (PERC) currently have the highest share in the photovoltaic market. However, heterojunction (HJT) and tunnel oxide passivated contact (TOPCon) solar cells are expected to gain significant market share shortly. Despite technological advancements, concerns about the reliability of HJT and TOPCon technologies when deployed in the field still need to be addressed. This work investigates the impact of sodium chloride (NaCl) on damp-heat-induced degradation in bifacial HJT, PERC, and TOPCon solar cells by exposing the solar cells to NaCl before damp heat (DH) testing. It is found that among all investigated cell technologies, TOPCon solar cells degrade the most with maximum power (P max ) loss of up to ∼75% rel , followed by HJT (P max drops ∼50% rel ), and PERC cells (P max drops only ∼10% rel ) after 20 h of DH testing, mainly attributed to an increase in R s on the front side of TOPCon cells, both sides of HJT cells and the rear side of PERC cells. The front of the PERC and the rear of the TOPCon solar cell are found to be stable. The rise in R s is attributed to the corrosion of the metal contact, which is caused by a high amount of Na + and Cl − ions penetrating the metal contact. This corrosion leads to increased porosity, detachment of the contact from the silicon interface, and increased recombination loss in some cases. These results are crucial for all cell technologies as they highlight the potential failures that could occur in the field. Na + and/or Cl − ions are common contaminants present in solar glass, human fingerprints, soldering flux, rainwater, soil/dust, and seawater. During field operation, these ions have the potential to penetrate and directly interact with solar cells. In our view, the preferred solution is for the solar cells to be corrosion-resistant, which can be rapidly assessed using the method presented in this work.

Potential‐free Sodium‐induced Degradation of Silicon Heterojunction Solar Cells

Addressing sodium ion-related degradation in SHJ cells by the application of nano-scale barrier layers

Highly crystallized tungsten doped indium oxide film stabilizes silicon heterojunction solar cells in sodium environment

Anionic Aggregates Induced Interphase Chemistry Regulation Toward Wide-Temperature Silicon-Based Batteries

Prevention of potential‐induced degradation using a moisture barrier in crystalline silicon photovoltaic modules

N-type nc-SiOx:H film enables efficient and stable silicon heterojunction solar cells in sodium environment

Reduction of Potential-Induced-Degradation of p-Type PERC Solar Cell Modules by an Ion-Diffusion Barrier Layer Underneath the Front Glass

Electro-analytical investigation of potential induced degradation in mc-silicon solar cells: case of sodium ion induced inductive loop

Mechanism Analysis of Potential-Induced Degradation of P-type Crystalline Si Solar Cells

Accelerated damp-heat testing at the cell-level of bifacial silicon HJT, PERC and TOPCon solar cells using sodium chloride

Microscopic mechanism for light-induced degradation of silicon solar cell in water vapor environment

Balance of efficiency and stability of silicon heterojunction solar cells

Short wavelength photons destroying Si‐H bonds and its influence on high efficiency silicon solar cells and modules

Sodium Diffuses from Glass Substrates through P1 Lines and Passivates Defects in Perovskite Solar Modules

Transparent Conductive Oxide Sputtering Damage on Contact Passivation in Silicon Heterojunction Solar Cells with Hydrogenated Nanocrystalline Silicon

Investigation of Potential‐Induced Degradation and Recovery in Perovskite Minimodules

Reassessment of silicon heterojunction cell performance under operating conditions

Diffusion and Drift of Sodium Ions in PID-affected Mono-Crystalline Silicon Solar Modules

Influence of intrinsic amorphous silicon passivation layer on the dark-state stability of SHJ cells

Reducing Potential Induced Degradation of Silicon Solar Cells by Using a Liquid Oxidation Technique

Hydrogen-induced degradation dynamics in silicon heterojunction solar cells via machine learning