Abstract:In order to obtain softer polyolefins applicable as toughener for polypropylene (PP), a series of in-reactor alloys composed of polyethylene, crystalline ethylene-propylene copolymer (cEP) and amorphous ethylene-propylene copolymer (aEP) were synthesized by sequential ethylene polymerization followed by ethylene-propylene copolymerization in periodic switching polymerization process (PSPP) using a spherical MgCl2-supported Ziegler-Natta catalyst. In the PSPP step, ethylene-propylene copolymerization was repeatedly switched between two different monomer feed ratios: one with high propylene/ethylene ratio to form aEP component, and the other with low propylene/ethylene ratio to form cEP component. In the synthesized PE/cEP/aEP in-reactor alloys, aEP accounted for 40∼56 wt.%, and cEP accounted for 18∼30 wt.% of the alloy. With aEP content rising above 48 wt.%, the alloys showed rather low modulus, and no yielding appeared in their stress-strain curve, implying that they were a sort of elastomeric material. By blending the PE/cEP/aEP alloys with isotactic PP, their PP-toughening performances were evaluated and compared with a commercial EPDM. Impact strength of PP toughened by the alloy was significantly higher than that toughened by EPDM at the same blend ratio. Cryo-fractured surface of PP/alloy blends showed that the alloy particles were uniformly dispersed in PP matrix, and showed a core-shell type morphology, in which the core domain was composed of polyethylene, and aEP constituted the shell domain in between the core and the PP matrix. Segmented EP copolymer chains (s-EP) located inside the aEP domains formed thin filaments bridging the core and the PP matrix, which are believed to act as compatibilizer that significantly enhanced interfacial adhesion between the PP matrix and the dispersed phase.

Regulation of Structure and Mechanical Properties of Poly(propylene-Butene) Alloys by Monomer Composition Switching

Research on Toughening Modification of Copolymerized Polypropylene Using Polyolefin Elastomers

Enhancement on the properties of polypropylene using bamboo particles: Effect of particle sizes and loadings

Characterization of Microstructure of Polypropylene Alloys

Polyethylene/crystalline ethylene-propylene copolymer/amorphous ethylene-propylene copolymer in-reactor alloys synthesized by periodic switching polymerization process: An excellent toughener for polypropylene

A New Approach to Fabricate Polypropylene Alloy with Excellent Low-Temperature Toughness and Balanced Toughness-Rigidity Through Unmatched Thermal Expansion Coefficients Between Components

Microstructure analysis of polypropylene reactor alloy

Influence of Polymerization Conditions on the Structure and Properties of Polyethylene/polypropylene In‐reactor Alloy Synthesized in the Gas Phase with a Spherical Ziegler–Natta Catalyst

Chain structure and mechanical properties of polyethylene/polypropylene/poly(ethylene-co-propylene)in-reactor alloys synthesized with a spherical Ziegler-Natta catalyst by gas-phase polymerization

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

THE STUDY OF APPLIED BEHAVIOR OF PP/PA6 BY USING GRAFTED POLYPROPYLENE AS COMPATILIZER

Study of Polypropylene Reactor Alloying

Synthesis of Polypropylene/poly(ethylene-co-propylene) In-Reactor Alloys by Periodic Switching Polymerization Process: Dynamic Change of Gas-Phase Monomer Composition and Its Influences on Polymer Structure and Properties

Effect of the synergistic interaction of zinc adipate, hydrotalcite and ethylene propylene rubber on the performances of polypropylene

Influence of Copolymerization Conditions on the Structure and Properties of Polyethylene/Polypropylene/Poly(Ethylene-Co-Propylene) In-Reactor Alloys Synthesized in Gas-Phase with Spherical Ziegler-Natta Catalyst

Effect of the Structure on the Morphology and Spherulitic Growth Kinetics of Polyolefin In‐reactor Alloys

Structural Parameters in Relation to the Rheological Behavior and Properties of PP/EPR In‐reactor Alloy Synthesized by Multi‐stage Sequential Polymerization

Synthesis of High Quality PE/PP In-Reactor Alloys with PE Matrix by Multi-Stage Polymerization

Improvement Of Structure And Properties Of Polypropylene/Poly(Ethylene-Co-Propylene) In-Reactor Alloy By Modifying The Cocatalyst

Morphology and properties of PP in-reactor alloys prepared with a MgCl2/TiCl4/diisobutyl phthalate/phosphate tris-methylphenyl ester catalyst system

Interface Physical Influence on Mechanic Properties of PP/AS Modified Polymer Caused by Maleic Anhydride