Abstract:In order to obtain softer polyolefins applicable as toughener for polypropylene (PP), a series of in-reactor alloys composed of polyethylene, crystalline ethylene-propylene copolymer (cEP) and amorphous ethylene-propylene copolymer (aEP) were synthesized by sequential ethylene polymerization followed by ethylene-propylene copolymerization in periodic switching polymerization process (PSPP) using a spherical MgCl2-supported Ziegler-Natta catalyst. In the PSPP step, ethylene-propylene copolymerization was repeatedly switched between two different monomer feed ratios: one with high propylene/ethylene ratio to form aEP component, and the other with low propylene/ethylene ratio to form cEP component. In the synthesized PE/cEP/aEP in-reactor alloys, aEP accounted for 40∼56 wt.%, and cEP accounted for 18∼30 wt.% of the alloy. With aEP content rising above 48 wt.%, the alloys showed rather low modulus, and no yielding appeared in their stress-strain curve, implying that they were a sort of elastomeric material. By blending the PE/cEP/aEP alloys with isotactic PP, their PP-toughening performances were evaluated and compared with a commercial EPDM. Impact strength of PP toughened by the alloy was significantly higher than that toughened by EPDM at the same blend ratio. Cryo-fractured surface of PP/alloy blends showed that the alloy particles were uniformly dispersed in PP matrix, and showed a core-shell type morphology, in which the core domain was composed of polyethylene, and aEP constituted the shell domain in between the core and the PP matrix. Segmented EP copolymer chains (s-EP) located inside the aEP domains formed thin filaments bridging the core and the PP matrix, which are believed to act as compatibilizer that significantly enhanced interfacial adhesion between the PP matrix and the dispersed phase.

Polyethylene/crystalline ethylene-propylene copolymer/amorphous ethylene-propylene copolymer in-reactor alloys synthesized by periodic switching polymerization process: An excellent toughener for polypropylene

Regulation of Structure and Mechanical Properties of Poly(propylene-Butene) Alloys by Monomer Composition Switching

Research on Toughening Modification of Copolymerized Polypropylene Using Polyolefin Elastomers

Enhanced Multiphase Interfacial Interaction of Impact Polypropylene Copolymer by In-Situ Introducing Polyethylene

Preparation of PBT/POE‐g‐GMA/PP Ternary Blends with Good Rigidity–toughness Balance by Core–shell Particles

A New Approach to Fabricate Polypropylene Alloy with Excellent Low-Temperature Toughness and Balanced Toughness-Rigidity Through Unmatched Thermal Expansion Coefficients Between Components

Toughening Mechanism of Polypropylene Bends with Polymer Particles in Core-Shell Structure: Equivalent Rubber Content Effect Related to Core-Shell Interfacial Strength

Chain structure of polyethylene/polypropylene in-reactor alloy synthesized in gas phase with spherical Ziegler–Natta catalyst

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

Toughening with Little Rigidity Loss and Mechanism for Modified Polypropylene by Polymer Particles with Core–shell Structure

Preparation and Characterization of High MFR Polypropylene and Polypropylene/poly(ethylene‐co‐propylene) In‐reactor Alloys

Chain structure and mechanical properties of polyethylene/polypropylene/poly(ethylene-co-propylene)in-reactor alloys synthesized with a spherical Ziegler-Natta catalyst by gas-phase polymerization

Combined effects of matrix molecular weight and crystallinity on the impact toughness of PP/EPR blends: The role of chain entanglement

Morphology and properties of PP in-reactor alloys prepared with a MgCl2/TiCl4/diisobutyl phthalate/phosphate tris-methylphenyl ester catalyst system

Balanced toughening and strengthening of ethylene–propylene rubber toughened isotactic polypropylene using a poly(styrene-b-ethylene–propylene) diblock copolymer

Synthesis of Polypropylene/poly(ethylene-co-propylene) In-Reactor Alloys by Periodic Switching Polymerization Process: Dynamic Change of Gas-Phase Monomer Composition and Its Influences on Polymer Structure and Properties

Fabrication Of Polypropylene Blends With Excellent Low-Temperature Toughness And Balanced Toughness-Rigidity By A Combination Of Epr And Seeps

Realizing Simultaneous High‐temperature Strength and Low‐temperature Elongation in Polyolefin Elastomer Toughened Polypropylene Via Controlling the Dispersed Phase Size

Toughening of Polypropylene Highly Filled with Aluminum Hydroxide

Chain microstructure of two in-reactor alloy impact polypropylene resins with same stiffness and different toughness

Investigation of Crystallization, Morphology, and Mechanical Properties of Polypropylene/Polypropylene-Polyethylene Block Copolymer Blends