Abstract:Using triethylaluminum (TEA), triisobutylaluminum (TIBA) or TEA/TIBA mixtures of molar ratio 75/25, 50/50 and 25/75 as the cocatalyst, five different ethylene–propylene copolymer samples were synthesized by a MgCl2/SiO2/TiCl4/diester type Ziegler–Natta catalyst in a slurry polymerization process. The synthesized copolymers are strongly heterogeneous in chain structure and were fractionated into part of nearly random copolymer and part of segmented copolymer. Both polymerization activity and copolymer structure were found to be markedly changed when the cocatalyst was changed from TEA to TEA/TIBA mixtures or pure TIBA. As the content of TEA in cocatalyst increases, yield of the random part of product increases and the yield of the crystalline segmented copolymer part decreases. There is also a decrease in ethylene content of the whole product with increasing TEA amount. Copolymerization behaviors of the TEA/TIBA mixture activated catalysis systems are not simple superposition of those activated by pure TEA and TIBA. When a 50/50 TEA/TIBA mixture was used as cocatalyst, the copolymerization activity became the highest, and yields of both the random copolymer part and the segmented copolymer part are close to the highest level. On the other hand, both parts of the copolymer produced with a 50/50 TEA/TIBA mixture are relatively more blocky than the products of TEA or TIBA systems, and difference in ethylene content between the random part and the segmented part was the smallest. The segmented copolymer part of three typical samples was further fractionated by temperature-gradient extraction fractionation into fractions of different ethylene content and sequence distribution. Changing TEA content in the cocatalyst exerted strong influences also on the fraction distribution of the segmented part of copolymer.

Improvement Of Structure And Properties Of Polypropylene/Poly(Ethylene-Co-Propylene) In-Reactor Alloy By Modifying The Cocatalyst

Regulation of Structure and Mechanical Properties of Poly(propylene-Butene) Alloys by Monomer Composition Switching

Influence Of Cocatalyst On The Structure And Properties Of Polypropylene/Poly (Ethylene-Co-Propylene) In-Reactor Alloys Prepared By Mgcl2/Ticl4/Diester Type Ziegler-Natta Catalyst

Regulating the Structure of Ethylene-Propylene Copolymer for Polyolefin In-Reactor Alloy with Improved Properties

Advanced Catalyst Technology for Broad/Bimodal Polyethylene, Achieved by Polymer-Coated Particles Supporting Hybrid Catalyst

Polypropylene and Ethylene−Propylene Copolymer Reactor Alloys Prepared by Metallocene/Ziegler−Natta Hybrid Catalyst

Improving Microisotacticity of Ziegler–Natta Catalyzed Polypropylene by Using Triethylaluminum/triisobutylaluminum Mixtures As Cocatalyst

Enhanced Multiphase Interfacial Interaction of Impact Polypropylene Copolymer by In-Situ Introducing Polyethylene

Research on Toughening Modification of Copolymerized Polypropylene Using Polyolefin Elastomers

Preparation of Polypropylene/MMT Nanocomposites Using Complex Supported Catalysts

Influence of Copolymerization Conditions on the Structure and Properties of Polyethylene/Polypropylene/Poly(Ethylene-Co-Propylene) In-Reactor Alloys Synthesized in Gas-Phase with Spherical Ziegler-Natta Catalyst

Chain structure and mechanical properties of polyethylene/polypropylene/poly(ethylene-co-propylene)in-reactor alloys synthesized with a spherical Ziegler-Natta catalyst by gas-phase polymerization

High temperature polymerization of propylene catalyzed by MgCl2-supported Ziegler–Natta catalyst with various cocatalysts

Influence of Polymerization Conditions on the Structure and Properties of Polyethylene/polypropylene In‐reactor Alloy Synthesized in the Gas Phase with a Spherical Ziegler–Natta Catalyst

Influence of Cocatalyst on High Temperature Polymerization of Propylene Catalyzed by Ziegler-Natta Catalyst

Influnences of mixed cocatalyst on propylene bulk polymerization

Strong Influences of Cocatalyst on Ethylene/propylene Copolymerization with a MgCl2/SiO2/TiCl4/diester Type Ziegler–Natta Catalyst

Highly active Ziegler-Natta Catalysts for propylene polymerization (2) effects of Al/Ti ratio and polymerization temperature

Chain structure of polyethylene/polypropylene in-reactor alloy synthesized in gas phase with spherical Ziegler–Natta catalyst

Structure and Properties of Ethylene/propylene Copolymers Synthesized with Bis(2,4,7-Trimethylindenyl)zirconium Dichloride Activated by Methyl Aluminoxanes Containing Different Amount of Trimethylaluminum

Combination of 8‐aminoquinoline Nickel Dichloride and Cp2ZrCl2 Catalysts for Ethylene Polymerization