Abstract:The PP alloy was synthesized directly in the reactor with a 4(th) generation Ziegler-Natta catalyst. it is very different from mechanically blended PP alloys, its properties, especially its impact strength,are superior to those of the latter. However,so far the studies on the stucture of this kind of PP alloys have not been reported. The microstructure of a PP alloy was characterized by IR,DSC,and C-13-NMR. The sample was first fractionated and 8 fractions were obtained. The IR analysis showed that the ethylene content of each fraction is different. Except for the first fraction,which is an elastomer, the others are all hard powders at room temperature. Therefore, the fractions above 50 degreesC perhaps are all composed of ethylene-propylene block copolymers. DSC analysis showed that the melting curve of the PP alloy became broadened compared with that of i-PP,and a small peak appeared at 120 degreesC. The extracts of PP alloy in boiling heptane and every fractions of PP alloy all exhibited many small peaks. These peaks demonstrated that the macromolecular chains in PP alloy are composed of ethylene-propylene blocks,whose sequence length are very different. The C-13-NMR spectrum of fraction at 90 degreesC, similar to other fractions at 50 similar to 100 degreesC,also indicated that there are long ethylene sequences in macromolecualr chains of PP alloy. According to the above analysis,a conclusion was reached that the E-P copolymer in PP alloy is composed of EPR and E-P blocks,with different ethylene sequence length. This polydispersity structure in PP alloy made it possess very high impact property.

Regulating the Structure of Ethylene-Propylene Copolymer for Polyolefin In-Reactor Alloy with Improved Properties

Engineering Ethylene/1-Hexene Copolymers from Ethylene Stock with a Model-Guided Catalyst Feeding Policy

Regulation of Structure and Mechanical Properties of Poly(propylene-Butene) Alloys by Monomer Composition Switching

Polypropylene and Ethylene−Propylene Copolymer Reactor Alloys Prepared by Metallocene/Ziegler−Natta Hybrid Catalyst

Influence of Copolymerization Conditions on the Structure and Properties of Polyethylene/Polypropylene/Poly(Ethylene-Co-Propylene) In-Reactor Alloys Synthesized in Gas-Phase with Spherical Ziegler-Natta Catalyst

Improvement Of Structure And Properties Of Polypropylene/Poly(Ethylene-Co-Propylene) In-Reactor Alloy By Modifying The Cocatalyst

Control of Diffusion/Barrier Effects of Polymer-Coated Particles and the Strengthening of Ethylene Polymerization Reactor

Fe(acac)n and Co(acac)n bearing different bis(imino)pyridine ligands for ethylene polymerization and oligomerization

I-Pp/epr REACTOR ALLOY PREPARED THROUGH ETHYLENE/PROPYLENE SLURRY COPOLYMERIZATION CATALYZED BY METALLOCENE SUPPORTED Ipp PARTICLES

Influence of Polymerization Conditions on the Structure and Properties of Polyethylene/polypropylene In‐reactor Alloy Synthesized in the Gas Phase with a Spherical Ziegler–Natta Catalyst

Structure and Morphology of Polyethylene/polypropylene In‐reactor Alloys Synthesized by Spherical High‐yield Ziegler–Natta Catalyst

Effect of the Structure on the Morphology and Spherulitic Growth Kinetics of Polyolefin In‐reactor Alloys

Study of Polypropylene Reactor Alloying

Morphology and properties of PP in-reactor alloys prepared with a MgCl2/TiCl4/diisobutyl phthalate/phosphate tris-methylphenyl ester catalyst system

Characterization of Microstructure of Polypropylene Alloys

Influence Of Cocatalyst On The Structure And Properties Of Polypropylene/Poly (Ethylene-Co-Propylene) In-Reactor Alloys Prepared By Mgcl2/Ticl4/Diester Type Ziegler-Natta Catalyst

Fractionation and Characterization of an Ethylene–propylene Copolymer Produced with a MgCl2/SiO2/TiCl4/diester‐type Ziegler–natta Catalyst

Combination of 8‐aminoquinoline Nickel Dichloride and Cp2ZrCl2 Catalysts for Ethylene Polymerization

Synthesis of Polyethylene with Bimodal Molecular Weight Distribution by Supported Iron‐based Catalyst

Microstructure analysis of polypropylene reactor alloy

Influence of polymerization conditions on the chain structure of ethylene-propylene copolymer prepared by MgCl_2/TiCl_4 catalyst