Abstract:In this work, Cu 2+ / Zn 2+ co-substitution ceramics Ca(Cu <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">1/2</inf> Zn <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">1/2</inf> ) <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">x</inf> Mg <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">1–x</inf> Si <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">6</inf> (0 ≤ x ≤ 0.025) were prepared via the traditional solid phase reaction method. Cu 2+ and Zn 2+ ions occupied the position of Mg 2+ , resulting in a change in the crystal structure. In-depth discussion was had regarding the effects of co-substitution of Cu 2+ and Zn 2+ on dielectric properties. XRD diffraction pattern indicated that pure phase CaMgSi <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">6</inf> ceramics were obtained at x=0.02. Rietveld refinement results showed crystal structure information. A solid solution of Cu 2+ / Zn 2+ was formed inside the crystal lattice. Appropriate $\text{Cu}_{1/2}\text{Zn}_{1/2}^{2+}$ ions promoted sintering and grain growth. Density had a great effect on ε <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">r</inf> . Regarding the Q × f values, the external loss was crucial. The τ <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">f</inf> was associated with MgO <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">6</inf> octahedral distortion. Additionally, The optimal microwave dielectric properties were achieved by sintered CaMg <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.98</inf> (Cu <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">1/2</inf> Zn <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">1/2</inf> ) <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">0.02</inf> Si <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf> O <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">6</inf> ceramics at 1200 ◦ C : ε <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">r</inf> = 7.997, Q × f = 45107 GHz, τ <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">f</inf> = −42.52 ppm/°C In the terahertz range, the ceramic had decent dielectric properties: ε <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">r</inf> = 5.28, tanδ = 0.125.

Microwave dielectric properties and high frequency dielectric characteristic of Cu<sup>2+</sup>/ Zn<sup>2+</sup> co-substitution CaMgSi<sub>2</sub>O<sub>6</sub> ceramics

Structure Dependence of Microwave Dielectric Properties in Zn2-xSiO4-x-xCuO Ceramics

Structure dependence of microwave dielectric properties in Zn2-SiO4--xCuO ceramics

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Influence of CuO additive on phase formation, microstructure and microwave dielectric properties of Cu-doped CuxZn1.8-xSiO3.8 ceramics

Microwave dielectric characteristics of ceramics in Mg2SiO4–Zn2SiO4 system

Effects of Cu2+substitution on bond characteristics, Raman spectra, and microwave dielectric properties of Li2Mg0.6Zn0.4SiO4 ceramics

Phase Composition, Crystal Structure and Microwave Dielectric Properties of Mg2−Cu SiO4 Ceramics

Raman, complex chemical bond and structural studies of novel CaMg1-x(Mn1/2Zn1/2)xSi2O6 (x=0-0.1) ceramics

Microwave Dielectric Properties and Microstructure of (li<sub>2</sub>zn<sub>3−</sub><i><sub>x</sub></i>ti<sub>4−</sub><i><sub>x</sub></i>o<sub>12−3</sub><i><sub>x</sub></i>)–<i>x</i>catio<sub>3</sub> Ceramics (<i>x</i> = 0 to 0.32)

Improved Microwave Dielectric Properties of CaMgSi2O6 Ceramics Through CuO Doping

Synthesis, Phase Composition and Modified Microwave Dielectric Properties of Mg2+ Substituted Zn2SiO4 Ceramics with Uniform Microstructure

Effects of Cu Substitution on Microstructures and Microwave Dielectric Properties of Li2ZnSiO4 Ceramics

Microstructure evolution, crystal structure, Raman analysis, bond characteristics and enhanced microwave dielectric properties of Zn1-Cu ZrNb2O8 solid solution ceramics

Composite Dielectrics (1−x)(mg0.97zn0.03)2(ti0.95sn0.05)o4−xcatio3 Suitable for Microwave Applications

Structure and microwave dielectric properties of CaZr0.99−x(Zn1/3Nb2/3)xTi0.01O3 (0 ≤ x ≤ 0.2) microwave dielectric ceramics

Structure and Microwave Dielectric Properties of (zn1/3nb2/3)4+ Co-Substituted MgTiO3 Ceramic

Low-temperature Sintering and Microwave Dielectric Properties of (zn1−xcox)2sio4 Ceramics

High-Qf value and temperature stable Zn2+-Mn4+ cooperated modified cordierite-based microwave and millimeter-wave dielectric ceramics

Ultra‐high Quality Factor of (zn2/3nb1/3)3+ Co‐substitution MgAl2O4 Microwave Dielectric Ceramics

The Influence of Cu Substitution on the Microwave Dielectric Properties of Bazn2ti4o11 Ceramics