Abstract:Incorporating two-dimensional (2D) diamond nanosheets with fluorescent color centers exhibits great potential in the application of quantum sensing. However, color centers always show poor optical emission in chemical-vapor-deposited (CVD) diamond nanomaterials. To address this issue, Si doped diamond/graphite hybrid films were successfully fabricated in microwave-plasma CVD device. The films consist of diamond-core/graphite-shell nanosheets with high amount of diamond nanocrystalline particles. Two post treatments of acid oxidation and annealing in air were used to tailor photoluminescence (PL) of silicon-vacancy (SiV) centers. The SiV centers in the oxidized samples exhibit small PL increase compared with the as-deposited samples with SiV PL quenching. It is found that the graphite phase is selectively etched away with the presence of nanocrystalline diamond particles during the treatment of acid oxidation while the nanocrystalline diamond particles are efficiently removed with the presence of graphite using the air annealing method. Based on this result, a two-step approach of acid oxidation followed by air annealing was conducted to etch the non-diamond phase, forming diamond nanosheets. The SiV centers exhibit significant PL enhancement with a maximum value of 28 folds, compared with the single-step oxidized samples. The Raman and XPS results reveal that such PL increase originates from direct bonding of oxygen on the sp 3 carbon. Therefore, our work provides a feasible approach to prepare 2D diamond nanosheets with high-brightness color centers.

High-quality Diamond Microparticles Containing SiV Centers Grown by Chemical Vapor Deposition with Preselected Seeds

Large-scale Fabrication of High-Density Silicon-vacancy Centers via Helium-ion Implantation of Diamond Nucleation Surface

Fabrication of Diamond Nanoneedle Arrays Containing High‐Brightness Silicon‐Vacancy Centers

Varying temperature and silicon content in nanodiamond growth: effects on silicon-vacancy centers

Enhanced Nucleation and Growth of Diamond Film on Si by CVD Using a Chemical Precursor

Low-Temperature Growth Of Ultra-Thin Nano-Crystalline Diamond Films By Hfcvd In A Ch4/H-2 Mixture

Fabrication and characterization of high quality micro diamonds by hot filament CVD

Nano-crystalline Diamond Films Synthesized at Low Temperature and Low Pressure by Hot Filament Chemical Vapor Deposition

Vertical-Substrate MPCVD Epitaxial Nanodiamond Growth

Preparation and Characterization of High Quality Micro/submicro Single Crystal Diamonds by Hot Filament CVD Method

Ultrathin Nanocrystalline Diamond Films with Silicon Vacancy Color Centers via Seeding by 2 nm Detonation Nanodiamonds

Tailoring optical emission of silicon-vacancy centers in two-dimensional diamond nanosheets via a two-step oxidation approach

Improving the creation of SiV centers in diamond via sub-μs pulsed annealing treatment

Formation Mechanism of SiV in Diamond from Unintentional Silicon Doping by Microwave Plasma Chemical Vapor Deposition

Fabrication of Diamond Submicron Lenses and Cylinders by ICP Etching Technique with SiO 2 Balls Mask.

Two-Photon Excitation of Silicon-Vacancy Centers in Nanodiamonds for All-Optical Thermometry with a Noise Floor of 6.6 Mk·hz–1/2

All-optical nanoscale thermometry based on silicon-vacancy centers in detonation nanodiamonds

High quality CVD single crystal diamonds grown on nanorods patterned diamond seed

Two-Photon Excitation of Silicon-Vacancy Centers in Nanodiamonds for All-Optical Thermometry with a Noise Floor of 6.6 mKmiddotHz-1/2

Very high growth rate chemical vapor deposition of single-crystal diamond.

Fabrication of Diamond Thin Films with High Quality on Microcylindrical Substrates