Abstract:NiPtAl coatings are widely used as overlaying coatings besides bondcoats for thermal barrier coating (TBC) systems within high temperature environment. Oxidaiton behavior of NiPtAl coatings is mainly contribution for the failure of TBC systems or overlaying coatings. An initial oxide layer growth characteristics play a key role in extending lifetime of TBC system or overlaying coatings. In this work, the oxidation experiments of the Pt modified aluminide coating on CMSX-4 Ni-based alloy were carried out at 1150 degrees C for 1 h in 80% Ar+20%O-2. The microstructures of oxide on the NiPtAl coatings are studied by OM, SEM, TEM and Raman spectroscopy. The results indicated that the oxide layer on the NiPtAl coatings included stable and met-stable Al2O3 after 1 h oxidation, and part of spalled oxide layer as well as pores within the oxide layer. The 0.5 mu m thickness whisker-like theta-Al2O3 could form on NiPtAl coating during the initially oxidation stage. At the initial oxidation stage theta-Al2O3 fastly grew which resulted beta-NiAl to gamma'-Ni3Al transformation. The Pt particles formed on the inter-surface between alpha-Al2O3 and theta-Al2O3 layer due to a less Pt solid solubility in gamma'-Ni3Al compared to beta-NiAl in the coating. Fast growth of initial Al2O3 could induce pores formation within the alumina layer. The pores and stress due to oxidation and phase transformation could decrease the alumina adherence, and at last result in the oxide spallation.

Synergistic Effect of Pt and Hf on the Early-Stage Oxidation Behaviour of NiAl Coating at 1000°C

Cyclic Oxidation Behaviour of Pt-doped Aluminide Coating on DZ125 Containing Hf

Influence of Pt on oxidation behavior of CoNiCrAlY alloy

Effect of Al content on the oxidation behavior of NiCoCrAlYHf alloys at 1100°C

Microstructure Analysis of Initial Alumina of Pt-Modified Aluminide Coatings on Ni-Based Alloy

Cyclic oxidation behavior of Pt modified NiCoCrAlYHfZr + AlNiY coating on a Ni-based single crystal superalloy

Pt-modification on the thermal cycling behavior of NiCoCrAlYTa coating: a case study

High-temperature performance of Pt-modified Ni-20Co-28Cr-10Al-0.5Y coating: Formation mechanism of Pt-rich overlayer and its effect on thermally grown oxide failure

Investigation on the microstructural evolution and oxidation resistance of Ru-doped NiAlHf coatings at 1200 °C

Effect of Al2O3 scales from pre-oxidation on the microstructural evolution and phase transition of NiAlHf coatings at 1200 °C

A comparative study on the oxidation behavior of Y-, Hf- and YHf-doped NiCoCrAl alloys: effect of reactive elements

Effects of coating growth mode on the oxidation behavior of a hybrid Pt/Ru-modified aluminide coating at 1200 °C

Effect of Y-doping on the microstructural evolution and oxidation resistance of NiAlHf coatings at 1200 °C

The influence of Hf content on oxide scale microstructure and HfO2 formation mechanisms in two-phase (γ' + β) Ni-Al alloys

Oxidation behavior of high Hf nickel-based superalloy in air at 900, 1000 and 1100°C

Effect of Pt on Stress Rupture Properties of Pt-Modified Nickel Aluminide Coatings at 1100 °C

The effect of Re and Hf interaction on the oxidation performance in ReHf co-doped NiAl coating

Enhancing long-term cyclic oxidation performance of a dual-phase PtAl coatings at 1200 °C by Ru modification

Impact of Pt/Al ratios on the cyclic oxidation and TCP precipitation of β-(Ni, Pt)Al coated superalloy at 1150 °C

Comparative study of the reactive elements effects on oxidation behavior of a Ni-based superalloy

Effect of Pt modification on hot corrosion resistance of NiCrAlYSi+AlY coating at 900 °C