Abstract:Hf, Y, and Ce (0.1 wt % each) were added in Ni-based superalloy, prepared by vacuum induction melting (VIM), and their effects on oxidation behavior were investigated after 300 h, over the temperature range 900–1100 °C. The surface of the oxide layer predominantly consisted of Al2O3 and NiO at 900 °C. At 1000 °C, most of the surface is covered by Al2O3 along with a small amount of NiAl2O4. However, at 1100 °C, the oxide layer's surface mainly formed of NiAl2O4 with plate-like α-Al2O3. It has been found that Hf produced excellent oxidation resistance and improved the scale adhesion to the alloy surface. On the other hand, Ce has a limited effect at high temperatures, and the scale adhesion is decreased with increasing oxidation time. From the analysis of oxidation kinetics and microstructure, it has been proposed that the dynamic segregation of reactive elements does not physically leads to the blocking of ions outward diffusion through Al2O3. The improvement in oxidation resistance of alumina forming alloys produced by reactive elements is explained based on ionic radii, chemical reactivity with alloying elements, and alteration in the alumina grain boundary's electronic properties.

The effect of Re and Hf interaction on the oxidation performance in ReHf co-doped NiAl coating

Effect of Substrate Characteristics on Interdiffusion Coefficients of Ni and Al Atoms in Β-Nial Phase of Aluminide Coatings

A comparative study on the oxidation behavior of Y-, Hf- and YHf-doped NiCoCrAl alloys: effect of reactive elements

Effect of Al content on the oxidation behavior of NiCoCrAlYHf alloys at 1100°C

The influence of Hf content on oxide scale microstructure and HfO2 formation mechanisms in two-phase (γ' + β) Ni-Al alloys

Effect of Hf as oxygen vacancy formation inhibitor on the oxidation behavior of Ni-28 W alloy

The importance of grain boundaries on the reactive elements effect in β-NiAlHf alloy

Investigation on the microstructural evolution and oxidation resistance of Ru-doped NiAlHf coatings at 1200 °C

Effect of Al content on the oxidation behavior of Y/Hf-doped AlCoCrFeNi high-entropy alloy

Influence of Aluminum and Rhenium on the Isothermal Oxidation Behavior of CoNiCrAlY Alloys

Effect of Y-doping on the microstructural evolution and oxidation resistance of NiAlHf coatings at 1200 °C

Synergistic Effect of Zr and Hf Alloying on Cross Fluvial Microstructure of CoCrFeNi Eutectic High-Entropy Alloys

Cyclic Oxidation Behaviour of Pt-doped Aluminide Coating on DZ125 Containing Hf

Effect of Al2O3 scales from pre-oxidation on the microstructural evolution and phase transition of NiAlHf coatings at 1200 °C

Surface Rumpling Behavior of Hf/Zr Single-Doped and Co-Doped β-NiAl Coatings during High-Temperature Cyclic Oxidation

Preparation and characterization of ReCr co-doped β-NiAl coating on a Ni-based single crystal superalloy

Microstructural evolution and element interdiffusion of NiAlHf and NiAlHfY coatings deposited on a Ni-based superalloy

Influence of Re on High Temperature Oxidation Behavior of MCrAIY Type Coating Alloys

Comparative study of the reactive elements effects on oxidation behavior of a Ni-based superalloy

Influence of Ho and Hf on the Microstructure and Mechanical Properties of NiAl and NiAl-Cr(Mo) Eutectic Alloy

Preparation and Enhanced Isothermal Oxidation Resistance of a Low Diffusivity NiRePtAl Single-Phase Coating