Abstract:CoNiCrAl alloys are widely used as bond coats for thermal barrier coating (TBC) at high operating temperature for energy conversion systems, especially turbine. However, the effect of reactive element (RE) on the oxidation behavior of CoNiCrAl alloys is still not uniform, thereby limiting the usage of the alloys. To study the effect of co-doped RE, the polished cast CoNiCrAlLa, CoNiCrAlHf and CoNiCrAlLaHf alloys were oxidized at 1100 degrees C in vacuum. Growth kinetics and adherence of oxide scales formed on above alloys were studied through comparing mass dynamics curves and tracer oxidation of the alloys. SEM, TG and XRD as well as secondary neutrals mass spectrometry (SNMS) were employed to study the microstructure and growth mechanism of the oxide layers. The results showed that a protective Al2O3 scale formed on the surface of CoNiCrAlLaHf alloy, and the Al2O3 scale showed a good adherence due to a pinning effect of the internal oxidation and less Ni(Co)Al2O4 formation. The Hf could suppress La enrichment at the oxide/alloy interface for the co-doped alloy. Oxygen inwards-diffusion along the oxide, which mainly controlled oxide scale growth, was observed when these three alloys oxidized in the atmospheres including tracer O-18. Enrichment of Cr, Co and Ni occurred at the outer part of oxide scale, and then decreased to a low level within the oxide layer. These Cr, Co and Ni enrichments could promote the Ni(Co)Al2O4 formation at the top of oxide scale for the single-doped alloys, which was detrimental to Al2O3 adherence properties.

Effect of Hf as oxygen vacancy formation inhibitor on the oxidation behavior of Ni-28 W alloy

Influence of Hf on the Structure, Thermal Stability and Oxidation Resistance of Ti-Al-N Coatings

A comparative study on the oxidation behavior of Y-, Hf- and YHf-doped NiCoCrAl alloys: effect of reactive elements

Effects of Hafnium and Yttirium on the Oxidation-Resistence of Ni3al/Crmob Alloy

Characteristics and formation mechanism of Hf inclusions in directionally casted Ni-based superalloy

The role of Dy and Hf doping on oxidation behavior of two-phase (γ′+β) Ni–Al alloys

Effect of Hf Addition on Initial Microstructure of (ni, Pt)Al Coating and Inhibiting the Detrimental Sulfur During High Temperature Exposure at 1150 °C

Effect of Al content on the oxidation behavior of NiCoCrAlYHf alloys at 1100°C

Effect of Y-doping on the microstructural evolution and oxidation resistance of NiAlHf coatings at 1200 °C

Oxidation behavior of high Hf nickel-based superalloy in air at 900, 1000 and 1100°C

The influence of Hf content on oxide scale microstructure and HfO2 formation mechanisms in two-phase (γ' + β) Ni-Al alloys

Co-doping Effect of Hf and Y on Improving Cyclic Oxidation Behavior of (ni,pt)al Coating at 1150 °C

High-temperature oxidation behavior of minor Hf doped NiAl alloy in dry and humid atmospheres

The effect of Re and Hf interaction on the oxidation performance in ReHf co-doped NiAl coating

Effect of Al content on the oxidation behavior of Y/Hf-doped AlCoCrFeNi high-entropy alloy

High-temperature Oxidation Behaviour of Minor Hf-doped Β-Nial Single Crystals in Dry and Humid Atmospheres

Effect of HfC addition on the microstructure and properties of W–4.9Ni–2.1Fe heavy alloys

Effects of Hf Additions on the Microstructures and Mechanical Properties of Ni-rich Ni55Ti45 Alloys

An approach to improve the oxidation resistance of a Ni-28W-6Cr alloy by hindering the oxygen vacancy-mediated oxidation

EFFECT OF La AND Hf DOPANT ON THE HIGH TEMPERATURE OXIDATION OF CoNiCrAl ALLOYS

Structural characteristics and high-temperature oxidation behaviour of nano-HfO2-doped thermal barrier coatings