Research on Electrochemical Behaviour of Reference Electrodes for Corrosion Test under High Hydrostatic Pressure for Simulating Deep-Sea

Qian Yu,Defa Wu,Hao Min,Yunxiang Ma,Yinshui Liu

DOI: https://doi.org/10.1016/j.jelechem.2022.116625

IF: 4.598

2022-01-01

Journal of Electroanalytical Chemistry

Abstract:The reference electrode is one of the most crucial parts of electrochemical testing. However, there is little research on the performance of the deep-sea reference electrode. In this work, three different deep-sea refer-ence electrodes were fabricated, high-purity zinc reference electrode and two kinds of Ag/AgCl reference elec-trode made by the pressed pellets and the electrolytic chlorination method. The effect of deep-sea hydrostatic pressure varying from 0 MPa to 80 MPa on the electrochemical behaviour in 3.5 wt% NaCl solution was inves-tigated. The potential stability test results showed that the three electrodes' potentials were relatively stable in the atmospheric environment. At 80 MPa, the potential of the zinc electrode was undulant, the maximum fluc-tuation range was 0.360 V, and its surface corrosion was severe. As the hydrostatic pressure increased to 80 MPa, the embryo body of the Ag/AgCl electrode prepared by the pressed pellets method became loose and infiltrated amounts of NaCl solution. The potential fluctuation reached 0.036 V. For the Ag/AgCl reference electrode produced by the electrolytic chlorination method, its potential fluctuation under high hydrostatic pressure was not significant, which was 0.003 V. The exchange current density obtained by polarization curve fitting reached 1.281 mA/cm2 at 80 MPa. The equivalent circuit fitted to the electrochemical impedance spec-troscopy indicated that the internal resistance increased slowly with the hydrostatic pressure. The highest value was only 1906 omega center dot cm2.