Ultrafast high-temperature sintering (UHS) of WC and WC-containing ZrB 2

Emanuele De Bona,Levent Karacasulu,Cekdar Vakifahmetoglu,Vincenzo M. Sglavo,Mattia Biesuz

DOI: https://doi.org/10.1016/j.jallcom.2024.174102

IF: 6.2

2024-03-18

Journal of Alloys and Compounds

Abstract:WC and ZrB 2 are refractory ceramics with excellent thermophysical properties and melting temperatures exceeding 2800°C. Both materials require the application of external pressure and long sintering times for their consolidation. In particular, commercially available ZrB 2 powders are intrinsically difficult to sinter and usually need long pre-processing steps such as high-energy ball milling. Ultrafast high-temperature sintering (UHS) is a recently developed technique that enables the consolidation of bulk ceramics within minutes. In the present work, pure WC was efficiently densified to above 98% in just 3 min by UHS. Moreover, small WC additions enhanced ZrB 2 densification by activating liquid phase sintering. Samples containing 5 and 10 vol% WC were sintered to 95 and 96%, respectively, in 2 min. All the WC initially present in the blend reacts to form a liquid phase during sintering and solidifies as WB and (Zr,W)C upon cooling. The formation of a ZrB 2 -(Zr,W)B 2 core-shell structure was detected in all the sintered composites. The hardness of UHS samples reaches 15 GPa (WC - ZrB 2 composites) and 21 GPa (pure WC), similar to that measured in materials obtained by slower and more sophisticated pressure-assisted sintering techniques.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering