Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Preparation and properties of zirconium diboride-based ultra-high temperature ceramics

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Microstructure and properties of silicon carbide whisker reinforced zirconium diboride ultra-high temperature ceramics

Preparation and Characterization of ZrB 2 -Sic Ultra-High Temperature Ceramics by Microwave Sintering

Processing and Mechanical Properties of Zirconium Diboride‐Based Ceramics Prepared by Spark Plasma Sintering

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Spark plasma sintering and hot pressing of ZrB2–SiCW ultra-high temperature ceramics

Enhanced Mechanical Properties and Oxidation Resistance of Zirconium Diboride Ceramics via Grain‐Refining and Dislocation Regulation

Characterization of hot-pressed short carbon fiber reinforced ZrB2–SiC ultra-high temperature ceramic composites

Effect of SiC Content on the Ablation and Oxidation Behavior of ZrB2-Based Ultra High Temperature Ceramic Composites

Preparation and Mechanical Properties of ZrB2-based Ceramics Using MoSi2 As Sintering Aids

Ultrahigh‐temperature tensile behaviors of ZrB2–SiC ceramics

Fabrication and mechanical properties of ZrB2–SiCw ceramic matrix composite

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Processing and Mechanical Properties of Short Carbon Fibers Toughened Zirconium Diboride-Based Ceramics

Effects of Short Carbon Fiber on Mechanical Properties of ZrB2-SiC Ultra-high Temperature Ceramics

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

Mechanical properties and fracture behavior of ultrahigh temperature ceramics at ultrahigh temperatures

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Preparation And Mechanical Properties Of Zirconium Diboride Matrix Composites Reinforced By Silicon Carbon Platelets

Effect of carbon nanotube on processing, microstructural, mechanical and ablation behavior of ZrB2-20SiC based ultra-high temperature ceramic composites