Fine‐Grain High‐Performance Densified Oxide Fibers Produced by Open Ultrafast High‐Temperature Sintering
Youmei Wang,Weiwei Qin,Zhao Chen,Zhezhe Deng,Dehua Ma,Yifan Wang,Xiaoqing Wang,Yunguang Yin,Yongshuai Xie,Benxue Liu,Luyi Zhu,Xinqiang Wang,Guanghui Zhang,Dong Xu
DOI: https://doi.org/10.1002/adma.202412139
IF: 29.4
2024-10-17
Advanced Materials
Abstract:Open ultrafast high‐temperature sintering (OUHS) in air, characterized by rapid heating/cooling (>10000 K min−1) and a short high‐temperature holding time ( 10000 K min−1) and a short high‐temperature holding time (<10 s), is used to produce 3 mol% yttria‐stabilized zirconia continuous fibers with coherent boundaries forming robust connections between fine grains. The tensile strength of these fibers (2.33 GPa on average, sintering temperature = 1673 K) notably exceeds that of their counterparts produced by traditional sintering (1.17 GPa). The effects of pores on fiber mechanical properties are analyzed using experimental and theoretical methods. For a versatility demonstration, OUHS is applied to several types of polycrystalline oxide fibers (HfO2, Al2O3, TiO2, Y2O3, and La2Zr2O7), considerably improving their mechanical properties and enabling crystalline phase control, which demonstrates the suitability of this procedure for the development of high‐performance materials.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology