Abstract:The mechanical strengths of silicon wafers are crucial for the manufacturing yield of integrated circuits (ICs), which have received intensive attention over the years. With reducing the feature size of ICs, the mechanical strengths of silicon wafers become more significant. Actually, the gliding of indentation dislocations on single-crystalline silicon wafers at a given temperature reflects the mechanical strengths of silicon wafers. Since the gliding of indentation dislocations is driven by the residual stress around the indentation, the investigation on the correlation between the residual stress and dislocation gliding is of significance. In this paper, we first use micro-Raman microscopy to characterize the relief of stress around the indentation due to the annealling at 300 or 500 ℃. Then the effect of such a relief-stress on the gliding of indentation dislocations at 700-900 ℃ is investigated. In the case without the prior stress-relief, the indentation dislocations glide to the maximum distance after 2 h annealling at 700-900 ℃. With the prior stress-relief due to the annealling at 300 or 500 ℃, the indentation dislocations can still glide to the maximum distance after 2 h annealling at 900 ℃, however the gliding velocity significantly decreases and the gliding distance is remarkably reduced after 2 h annealling at 700 or 800 ℃. Such a reduction of gliding distance is most significant in the case of 700 ℃ annealling following the stress-relief with the 500 ℃/2 h annealling. Despite the prior stress-relief, as long as the annealing time at 700 or 800 ℃ is sufficiently extended, the indentation dislocations can glide to the maximum distance. In view of the above results, it is believed that the maximum gliding distance of indentation dislocations at a given temperature is independent of the values of residual stress around the indentation provided that the residual stresses are larger than the critical stress for driving the dislocation movement. Nevertheless, the annealing time for achieving the maximum gliding distance at a given temperature should be remarkably extended as the residual stresses around the indentation are relieved.

Effects of Surface Stress Relaxation on Reflection Electron Microscopy Images of Normal Emerging Edge Dislocations

Reflection electron imaging of free surfaces and surface/dislocation interactions

Diffraction Contrast in Reflection Electron Microscopy—ii. Surface Steps and Dislocations under the Surface

Identification of Dislocations on Crystal Surfaces

Diffraction contrast in reflection electron microscopy—I. Screw dislocation

The Surface Step: Its Strain Field and REM Image Contrast Splitting

Effect of Prior Stress-Relief on the Gliding of Indentation Dislocations on Silicon Wafers

Preface of 16th International Conference on Defects, Recognition, Imaging and Physics in Semiconductors

Diffraction-Based Multiscale Residual Strain Measurements

Thermal diffuse scattering and REM image-contrast preservation

Reflection Electron Microscopy Observations of Dislocations and Dislocation Motion in Zinc Oxide

Line Stress of Step Edges at Crystal Surfaces

Surface relaxation and stress of fcc metals: Cu, Ag, Au, Ni, Pd, Pt, Al and Pb

Effect of sample thinning on strains and lattice rotations measured from Transmission Kikuchi diffraction in the SEM

Surface Resonance Effects and Beam Convergence in Rem

Elastic strain mapping of plastically deformed materials by TEM

The influence of surface stress on the equilibrium shape of strained quantum dots

Nanoindentation Stress Relaxation to Quantify Dislocation Velocity–Stress Exponent

Computer Simulation of Quantum Dot Surface under Stress

A REM study of inhomogeneous stress fields induced by the interfacial steps at In0.2Ga0.8As/GaAs interface

Importance of TEM sample thickness for measuring strain fields