Abstract:The development of high-speed aerial vehicles urgently requires high-performance integrated materials for ablation resistance, thermal insulation and oxidant protection under high temperature. The previously prepared carbon aerogel composites (C/CA), with ultra-high temperature thermal insulation properties, were impregnated with SiCO precursor sol and pyrolysed in nitrogen atmosphere at 1200?C. The impregnation/pyrolysis process was performed once, twice and thrice to obtain three different C/C-SiCO nanoporous ceramic composites. Further, TaSi2-MoSi2-borosilicate glass (TM-BG) coating or TaSi2-MoSi2-ZrB2-borosilicate glass (TMZBG) coating was prepared on the surface of the C/C-SiCO through slurry brushing combined with graphite powder embedded sintering process. By simulating the actual application environment through oxygen acetylene flame ablation test, the ablation resistance of the samples was studied and their oxidation mechanism was analysed. The results show that the ablation rate of the C/C-SiCO after 200 s ablation at 1600 ?C decreases with the increase of the number of impregnation/pyrolysis steps and that the ablation resistance of the coating modified C/C-SiCO was significantly enhanced. The addition of ZrB2 to the coating improves the compatibility between the substrates and the coating, and the TMZ-BG coated sample has better ablation resistance. At high temperature, the borosilicate glass in the coating is in a viscous flow state. Meanwhile the SiO2 generated by the oxidation of other silicide raw materials forms a dense glass layer on the coating surface, which can be used as an oxygen barrier to provide better protection for the substrates. The coating-modified C/C-SiCO porous ceramic composites are expected to be used as a high-temperature ablation-resistant material for the thermal protection system of new aerospace vehicles.

ABLATION PROPERTY OF <font>SiC-TaSi</font><sub>2</sub> COATED CARBON/CARBON COMPOSITES

Ablation resistance of SiC-modified nanocomposite ceramic coating prepared by LPDS method on titanium alloy

Effect of Si, Al2O3 additives on the ablation behavior of ZrB2-SiC coating with Al2O3-modified SiC bond coat for C/C composites

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Effect of tantalum carbide on the ablation behaviors of hafnium carbide coating for C/C composites under single and cyclic oxyacetylene torch environments

Ablation resistance of C/C-SiCo nanoporous ceramic composites with TaSi2-MoSi2-ZrB2-borosilicate glass coating

Preparation, Mechanical and Ablation Properties of a C/C-TaB2-SiC Composite

Anti-ablation performance of plasma sprayed ZrB 2 /SiC coatings on C/C substrates and the influence of a chemical vapor deposited SiC interlayer

TaSi2 modified HfB2‐SiC coating: preparation and ablation behavior

Anti-ablation Performance of Plasma Sprayed ZrB2/SiC Coatings on C/C Substrates and the Influence of a Chemical Vapor Deposited SiC Interlayer

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Ablation Resistance of C/C Composites with Atmospheric Plasma-Sprayed W Coating

Preparation and long-term ablation behavior of Cf-reinforced ZrC-SiC coated C/C-ZrC-SiC composite

Study on the ablation performance of SiC-coated high thermal conductivity three-dimensional C/C composites

ABLATION OF CARBON-CARBON COMPOSITES WITH TANTALUM

Oxidation ablation resistance of ZrB2-HfB2-SiC-TaSi2 coating prepared on C/C composite surface

UHTC coating reinforced by HfC nanowires against ablation for C/C composites

Ablation behavior of high-entropy boride (Hf-Zr-Ta-Ti)B 2 coating fabricated via supersonic atmospheric plasma spraying for carbon/carbon composites

MoSi2-HfC/TaC-HfC multi-phase coatings synthesized by supersonic atmospheric plasma spraying for C/C composites against ablation