Abstract:The development of high-speed aerial vehicles urgently requires high-performance integrated materials for ablation resistance, thermal insulation and oxidant protection under high temperature. The previously prepared carbon aerogel composites (C/CA), with ultra-high temperature thermal insulation properties, were impregnated with SiCO precursor sol and pyrolysed in nitrogen atmosphere at 1200?C. The impregnation/pyrolysis process was performed once, twice and thrice to obtain three different C/C-SiCO nanoporous ceramic composites. Further, TaSi2-MoSi2-borosilicate glass (TM-BG) coating or TaSi2-MoSi2-ZrB2-borosilicate glass (TMZBG) coating was prepared on the surface of the C/C-SiCO through slurry brushing combined with graphite powder embedded sintering process. By simulating the actual application environment through oxygen acetylene flame ablation test, the ablation resistance of the samples was studied and their oxidation mechanism was analysed. The results show that the ablation rate of the C/C-SiCO after 200 s ablation at 1600 ?C decreases with the increase of the number of impregnation/pyrolysis steps and that the ablation resistance of the coating modified C/C-SiCO was significantly enhanced. The addition of ZrB2 to the coating improves the compatibility between the substrates and the coating, and the TMZ-BG coated sample has better ablation resistance. At high temperature, the borosilicate glass in the coating is in a viscous flow state. Meanwhile the SiO2 generated by the oxidation of other silicide raw materials forms a dense glass layer on the coating surface, which can be used as an oxygen barrier to provide better protection for the substrates. The coating-modified C/C-SiCO porous ceramic composites are expected to be used as a high-temperature ablation-resistant material for the thermal protection system of new aerospace vehicles.

ABLATION OF CARBON-CARBON COMPOSITES WITH TANTALUM

Numerical analysis of ablative behavior of silicone resin coated carbon fabric

Ablation Analysis and Engineering Calculation on Carbon-based Material of Reentry Vehicles

Numerical analyses of ablative behavior of C/C composite materials

Ultra-high temperature ablation behavior of CVD-Hf 5 TaC 6 solid solution ceramic coating for C/C composites: Experiment and first-principle calculation

Analysis of thermochemical ablation and mechanical erosion of C/C composites based on macro-meso-scale numerical simulation methods

Modeling ablative behavior and thermal response of carbon/carbon composites

Effect of tantalum carbide on the ablation behaviors of hafnium carbide coating for C/C composites under single and cyclic oxyacetylene torch environments

Self‐defending mechanism of C/TaC‒SiC composites under 2100°C cyclic ablation environment

Research progress on tantalum carbide coatings oncarbon materials

Ablation behavior of high-entropy boride (Hf-Zr-Ta-Ti)B 2 coating fabricated via supersonic atmospheric plasma spraying for carbon/carbon composites

Numerical Simulation of C/C Composites Coupled Thermo-Mechanical Field under the Condition of High Temperatures and Ablation

Preparation, Mechanical and Ablation Properties of a C/C-TaB2-SiC Composite

Ablation-resistant Ta0.78Hf0.22C solid solution ceramic modified C/C composites for oxidizing environments over 2200 °C

Ablation and mechanical behaviour of C/C composites under an oxyacetylene flame and tensile loading environment

Ablation Behaviour of C/C–ZrC Composites in a Solid Rocket Motor Environment

Ablation behavior of Ta, TaC and Ta/TaC coatings on graphite under high-energy laser irradiation

Ablation resistance of C/C-SiCo nanoporous ceramic composites with TaSi2-MoSi2-ZrB2-borosilicate glass coating

Enhancing Ablation Resistance of TaB2-Based Ultra-High Temperature Ceramics by Mixing Fine TaC Particles and Dispersed Multi-Walled Carbon Nanotubes

Research and Engineering Computation of Ablation Character of Carbon Phenolic Aldehyde Composite Material

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites